Effect of ruthenium on tensile properties of a single crystal Ni-based superalloy | |
X. P. Tan ; J. L. Liu ; T. Jin ; Z. Q. Hu ; H. U. Hong ; B. G. Choi ; I. S. Kim ; C. Y. Jo | |
刊名 | Metals and Materials International |
2012 | |
卷号 | 18期号:5页码:769-775 |
关键词 | alloys solidification strength tensile test microstructure nickel-based superalloy temperature behavior mechanisms phase |
ISSN号 | 1598-9623 |
中文摘要 | The tensile properties of two single crystal Ni-based superalloys with and without added Ru (0 and 3 wt%) were investigated under a constant strain rate of 3.3x10(-4) /s at 20 A degrees C, 760 A degrees C, 800 A degrees C and 1000 A degrees C, respectively. The deformation mechanisms could be divided into two temperature regimes. From room temperature to 800 A degrees C, the deformation mechanism is caused by the shearing of gamma' particles by anti-phase boundaries (APB) or stacking faults. At 1000 A degrees C, the deformation mechanism is caused by the bypassing of gamma' particles by dislocations. At 20 A degrees C and 800 A degrees C, gamma' particles were sheared by APB. Due to smaller gamma' particles, the yield strength was decreased with addition of 3 wt% Ru. Additionally, work hardening is less pronounced in the alloy without Ru, hence the ultimate tensile strength was not decreased with the addition of 3 wt% Ru. At 760 A degrees C, gamma' particles were sheared by stacking faults. Since the formation of stacking faults was promoted, the yield strength was decreased due to a 3 wt% Ru addition. However, the ultimate tensile strength was significantly increased when 3 wt% Ru was added. This is due to the markedly stronger work hardening caused by large numbers of stacking faults. At 1000 A degrees C, deformation occurred by dislocations bypassing gamma' particles. Due to wider gamma channels, the yield strength was decreased by 3 wt% Ru addition. Moreover, Alloy 3Ru has smaller gamma' particles and a volume fraction as well as less pronounced work hardening, so the ultimate tensile strength was decreased when 3 wt% Ru was added. |
原文出处 | |
公开日期 | 2013-02-05 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/60252] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. P. Tan,J. L. Liu,T. Jin,et al. Effect of ruthenium on tensile properties of a single crystal Ni-based superalloy[J]. Metals and Materials International,2012,18(5):769-775. |
APA | X. P. Tan.,J. L. Liu.,T. Jin.,Z. Q. Hu.,H. U. Hong.,...&C. Y. Jo.(2012).Effect of ruthenium on tensile properties of a single crystal Ni-based superalloy.Metals and Materials International,18(5),769-775. |
MLA | X. P. Tan,et al."Effect of ruthenium on tensile properties of a single crystal Ni-based superalloy".Metals and Materials International 18.5(2012):769-775. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论