氢对锆基块体非晶合金形变和开裂的影响

CORC > 力学研究所 > 中国科学院力学研究所 > 力学所知识产出(1956-2008)

	氢对锆基块体非晶合金形变和开裂的影响
	单广斌; 魏炳忱; 李金许; 乔利杰; 褚武扬
刊名	金属学报=Acta Metallurgica Sinica
	2006-07-11
卷号	42 期号:7 页码:689-693
关键词	锆基块体非品合金原位拉伸氢 Zr base bulk amorphous alloy 剪切带 hydrogen shear band in situ tensile
ISSN号	041-1961
其他题名	Effects of Hydrogen on Shear Bands and Cracking in Zr Base Bulk Amorphous Alloy
通讯作者	单广斌
中文摘要	通过充氢和未充氢缺口拉伸试样和三点弯曲试样在SEM下的原位加载,研究了氢对Zr65Al7.5Ni10Cu17．5块体非晶合金形变和开裂过程的影响．结果表明,无论是否有氢,块体非晶的剪切带发展到临界尺寸,剪切裂纹就沿剪切带形核、扩展,它一旦张开就导致快速的断裂．断口边缘观察到的无特征区是剪切带,而不是剪切裂纹断口;剪切断口形貌和拉伸断口形貌没有本质区别．只有当长时间充氢才能形成氢鼓泡,如鼓泡很小或尚未形成,则氢对剪切带以及裂纹的形核、扩展没有明显影响;如存在较大的氢鼓泡,则当剪切带尚未充分发展时微裂纹就形核,导致低应力脆断．
英文摘要	The effects of hydrogen on shear bands and cracking in bulk amorphous alloy Zr65Al7.5Ni10Cu17.5 have been studied through in situ tensile single-edge notched samples and three-point bending smooth samples in SEM. The results show that for either hydrogen-free or hydrogenated samples, shear crack will initiate and propagate along shear bands when shear bands grow to a critical condition, and open finally, resulting in rapid fracture of samples. The characterless zone on the fracture surface is the shear band instead of fracture surface of shear crack. There is no essential difference between the morphologies of tensile fracture and shear surface. Hydrogen blistering will form after charging for a long time, and if the blistering is very small or unformed, there is no evident effect for forming of shear bands and initiating of crack. If the hydrogen blistering is large enough, the shear crack will initiate at early growing stage of shear band, resulting in brittle fracture under low stress.
研究领域[WOS]	Metallurgy & Metallurgical Engineering
关键词[WOS]	STRESS-CORROSION CRACKING; IN-SITU SEM; METALLIC-GLASS; PLASTIC-FLOW; EMBRITTLEMENT; FRACTURE; FAILURE; DAMAGE; TI
收录类别	SCI ; EI ; CSCD
语种	中文
CSCD记录号	CSCD:2482777
WOS记录号	WOS:000239402500003
公开日期	2009-08-03 ; 2010-08-20
内容类型	期刊论文
源URL	[http://dspace.imech.ac.cn/handle/311007/40958]
专题	力学研究所_力学所知识产出(1956-2008)
推荐引用方式 GB/T 7714	单广斌,魏炳忱,李金许,等. 氢对锆基块体非晶合金形变和开裂的影响[J]. 金属学报=Acta Metallurgica Sinica,2006,42(7):689-693.
APA	单广斌,魏炳忱,李金许,乔利杰,&褚武扬.(2006).氢对锆基块体非晶合金形变和开裂的影响.金属学报=Acta Metallurgica Sinica,42(7),689-693.
MLA	单广斌,et al."氢对锆基块体非晶合金形变和开裂的影响".金属学报=Acta Metallurgica Sinica 42.7(2006):689-693.