Mixed-mode fracture mechanisms near the fatigue threshold of aisi-316 stainless-steel | |
Gao HJ(高华健); Delosrios ER; Miller KJ | |
刊名 | Fatigue of Engineering Materials and Structures |
1983 | |
卷号 | 6期号:2页码:137-147 |
ISSN号 | 0160-4112 |
通讯作者 | HUA, G (reprint author), ACAD SINICA,INST MECH,BEIJING,PEOPLES R CHINA. |
合作状况 | 国内 |
中文摘要 | Near threshold, mixed mode (I and II), fatigue crack growth occurs mainly by two mechanisms, coplanar (or shear) mode and branch (or tensile) mode. For a constant ratio of ΔKI/ΔKII the shear mode growth shows a self-arrest character and it would only start again when ΔKI and ΔKII are increased. Both shear crack growth and the early stages of tensile crack growth, are of a crystallographic nature; the fatigue crack proceeds along slip planes or grain boundaries. The appearance of the fracture surfaces suggest that the mechanism of crack extension is by developing slip band microcracks which join up to form a macrocrack. This process is thought to be assisted by the nature of the plastic deformation within the reversed plastic zone where high back stresses are set up by dislocation pile-ups against grain boundaries. The interaction of the crack tip stress field with that of the dislocation pile-ups leads to the formation of slip band microcracks and subsequent crack extension. The change from shear mode to tensile mode growth probably occurs when the maximum tensile stress and the microcrack density in the maximum tensile plane direction attain critical values. |
类目[WOS] | Materials Science, Multidisciplinary |
研究领域[WOS] | Materials Science |
收录类别 | SCI |
原文出处 | http://dx.doi.org/10.1111/j.1460-2695.1983.tb00330.x |
语种 | 英语 |
WOS记录号 | WOS:A1983RK52800003 |
公开日期 | 2009-08-03 ; 2010-08-20 |
内容类型 | 期刊论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/39900] |
专题 | 力学研究所_力学所知识产出(1956-2008) |
推荐引用方式 GB/T 7714 | Gao HJ,Delosrios ER,Miller KJ. Mixed-mode fracture mechanisms near the fatigue threshold of aisi-316 stainless-steel[J]. Fatigue of Engineering Materials and Structures,1983,6(2):137-147. |
APA | Gao HJ,Delosrios ER,&Miller KJ.(1983).Mixed-mode fracture mechanisms near the fatigue threshold of aisi-316 stainless-steel.Fatigue of Engineering Materials and Structures,6(2),137-147. |
MLA | Gao HJ,et al."Mixed-mode fracture mechanisms near the fatigue threshold of aisi-316 stainless-steel".Fatigue of Engineering Materials and Structures 6.2(1983):137-147. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论