Deformation twinning and twinning-related fracture in nickel-base single-crystal superalloys during thermomechanical fatigue cycling | |
Sun, Fei; Zhang, Jianxin; Harada, Hiroshi | |
刊名 | ACTA MATERIALIA |
2014 | |
卷号 | 67页码:45-57 |
关键词 | Nickel-base superalloys Deformation twins Fracture Crack Thermomechanical fatigue (TMF) |
DOI | 10.1016/j.actamat.2013.12.011 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4800604 |
专题 | 山东大学 |
作者单位 | 1.Shandong Univ, Minist Educ, Key Lab Liquid Struct & Hered Mat, Jinan 250061, Shandong, Peoples R China. 2.[Zhang, Jianxin |
推荐引用方式 GB/T 7714 | Sun, Fei,Zhang, Jianxin,Harada, Hiroshi. Deformation twinning and twinning-related fracture in nickel-base single-crystal superalloys during thermomechanical fatigue cycling[J]. ACTA MATERIALIA,2014,67:45-57. |
APA | Sun, Fei,Zhang, Jianxin,&Harada, Hiroshi.(2014).Deformation twinning and twinning-related fracture in nickel-base single-crystal superalloys during thermomechanical fatigue cycling.ACTA MATERIALIA,67,45-57. |
MLA | Sun, Fei,et al."Deformation twinning and twinning-related fracture in nickel-base single-crystal superalloys during thermomechanical fatigue cycling".ACTA MATERIALIA 67(2014):45-57. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论