The effect of grinding on the sintering of raw petroleum coke | |
H. M. Cheng ; M. Liu ; Z. H. Shen ; J. Z. Xi ; H. Sano ; Y. Uchiyama ; K. Kobayashi | |
刊名 | Carbon
![]() |
1997 | |
卷号 | 35期号:7页码:869-874 |
关键词 | needle coke semicoke baking mechanical properties particle size graphite |
ISSN号 | 0008-6223 |
中文摘要 | Preparation of dense carbon materials without use of any binder was attempted, effect of grinding treatment on the characteristics of raw petroleum needle coke and on the properties of the sintered carbon compacts was investigated, and the sintering mechanizm of the coke after grinding was discussed. It was found that the coke particle size and crystalline size was decreased and the specific surface area of the coke was increased with grinding, and the influence was obvious up to 20 hours grinding treatment. The interlayer spacing of the coke after graphitization at 2773 K was gradually increased and the a-axis constant was marginally reduced with the grinding time. Results from the sintering experiment show that carbon materials can be sintered from the ground coke, and the density and flexural strength of the sintering compacts reached stable values of 1.8 g cm(-3) and about 70 MPa, respectively, after 20 hours grinding of the coke. The sintering ability of the coke after grinding was considered to result from the increase of surface energy, lattice distortion energy and fraction of volatile matters of the coke, which were induced by grinding treatment. (C) 1997 Elsevier Science Ltd |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/37945] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | H. M. Cheng,M. Liu,Z. H. Shen,et al. The effect of grinding on the sintering of raw petroleum coke[J]. Carbon,1997,35(7):869-874. |
APA | H. M. Cheng.,M. Liu.,Z. H. Shen.,J. Z. Xi.,H. Sano.,...&K. Kobayashi.(1997).The effect of grinding on the sintering of raw petroleum coke.Carbon,35(7),869-874. |
MLA | H. M. Cheng,et al."The effect of grinding on the sintering of raw petroleum coke".Carbon 35.7(1997):869-874. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论