Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O-2 plus water vapor at 500-700 degrees C

CORC > 金属研究所 > 中国科学院金属研究所

	Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O-2 plus water vapor at 500-700 degrees C
	Y. H. Shu ; F. H. Wang ; W. T. Wu
刊名	Oxidation of Metals
	1999
卷号	52 期号:5-6 页码:463-473
关键词	Ti60 alloy corrosion NaCl water vapor synergistic effect ni-cr alloys fe-cr oxidation steels
ISSN号	0030-770X
中文摘要	The corrosion behavior of Ti60 has bet 12 studied in oxygen containing water vapor at 500-700 degrees C, with and without a solid NaCl deposit on the surface. No measurable corrosion of the Ti60 alloy eas observed in atmospheres without NaCl. Corrosion of Ti60 was accelerated in the presence of NaCl because of the formation of a nonprotective TiO2 oxide scale, the corrosion of Ti60 is significantly aggravated due to the synergistic effect of NaCl and water vapor. When the temperature was increased up to the melting point of NaCl, the corrosion of Ti60 coated with NaCl both in air-NaCl and in O-2-NaCl plus water vapor became more severe. A mechanism to explain the effect of water vapor ann NaCl on the corrosion of Ti60 is proposed.
原文出处	://WOS:000082060400006
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/37482]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. H. Shu,F. H. Wang,W. T. Wu. Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O-2 plus water vapor at 500-700 degrees C[J]. Oxidation of Metals,1999,52(5-6):463-473.
APA	Y. H. Shu,F. H. Wang,&W. T. Wu.(1999).Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O-2 plus water vapor at 500-700 degrees C.Oxidation of Metals,52(5-6),463-473.
MLA	Y. H. Shu,et al."Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O-2 plus water vapor at 500-700 degrees C".Oxidation of Metals 52.5-6(1999):463-473.