Microstructure and superelasticity of severely deformed TiNi alloy | |
Z. C. Li ; X. K. Zhao ; H. Zhang ; L. Liu ; Y. B. Xu | |
刊名 | Materials Letters
![]() |
2003 | |
卷号 | 57期号:5-6页码:1086-1090 |
关键词 | Ti-50.4 at.%Ni alloy cold roll anneal superelasticity microstructure memory |
ISSN号 | 0167-577X |
中文摘要 | A Ti-50.4 at.%Ni alloy ingot was prepared and rolled into plate of 1-mm thickness at 1025 K. The hot-rolled plate was cold rolled at room temperature to the extent of 50% reduction in thickness and annealed at 573, 693 and 753 K, respectively. The investigated results revealed that 693 K annealed specimen had a homogeneous nanocrystalline structure with the grain size about 30 nm and showed the best superelasticity. The relation between the microstructure and the superelasticity has been discussed in the present report. (C) 2002 Elsevier Science B.V All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/35909] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Z. C. Li,X. K. Zhao,H. Zhang,et al. Microstructure and superelasticity of severely deformed TiNi alloy[J]. Materials Letters,2003,57(5-6):1086-1090. |
APA | Z. C. Li,X. K. Zhao,H. Zhang,L. Liu,&Y. B. Xu.(2003).Microstructure and superelasticity of severely deformed TiNi alloy.Materials Letters,57(5-6),1086-1090. |
MLA | Z. C. Li,et al."Microstructure and superelasticity of severely deformed TiNi alloy".Materials Letters 57.5-6(2003):1086-1090. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论