Microstructure characteristics of as-surface nanocrystallized 1420 aluminum alloy by high-energy shot peening | |
L. Q. Hu ; K. Wang ; G. Liu ; B. S. Xu | |
刊名 | Transactions of Nonferrous Metals Society of China |
2005 | |
卷号 | 15期号:3页码:615-618 |
关键词 | 1420 alloy aluminum alloy high-energy shot peening surface nanocrystallization microstructure microhardness low-carbon steel grain-refinement |
ISSN号 | 1003-6326 |
中文摘要 | A nanostructured surface layer was fabricated on 1420 aluminum alloy by high-energy shot peening. Microstructures were characterized by X-ray diffractometer(XRD), transmission electron microscope(TEM) and high-resolution electron microscope ( HRTEM), and microhardness measurement was conducted along the depth from top surface layer to matrix of the sample peened for 30 min. The results show that a nanocrystalline layer about 20 mu m in thickness is formed on the surface of the sample after high-energy shot peening, in which the grain size is changed from about 20 nm to 100 nm. In the surface layer of 20 - 50 mu m in depth, the microstructure consists of sub-micron grains. The surface nanocrystallization is accomplished by dislocation slip. The microhardness of the top surface nanostructured layer is enhanced obviously after high-energy shot peening(HESP) compared with that of the coarse-grained matrix. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/34873] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | L. Q. Hu,K. Wang,G. Liu,et al. Microstructure characteristics of as-surface nanocrystallized 1420 aluminum alloy by high-energy shot peening[J]. Transactions of Nonferrous Metals Society of China,2005,15(3):615-618. |
APA | L. Q. Hu,K. Wang,G. Liu,&B. S. Xu.(2005).Microstructure characteristics of as-surface nanocrystallized 1420 aluminum alloy by high-energy shot peening.Transactions of Nonferrous Metals Society of China,15(3),615-618. |
MLA | L. Q. Hu,et al."Microstructure characteristics of as-surface nanocrystallized 1420 aluminum alloy by high-energy shot peening".Transactions of Nonferrous Metals Society of China 15.3(2005):615-618. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论