Progressive damage during thermal shock cycling of D-gun sprayed thermal barrier coatings with hollow spherical ZrO2-8Y(2)O(3) | |
P. L. Ke ; Q. M. Wang ; J. Gong ; C. Sun ; Y. C. Zhou | |
刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
![]() |
2006 | |
卷号 | 435页码:228-236 |
关键词 | thermal barrier coatings detonation gun spraying failure mechanism stress distribution luminescence spectroscopy residual-stresses bond coats oxidation mechanisms evolution oxide instability spallation behavior failure |
ISSN号 | 0921-5093 |
中文摘要 | Thermal shock cycling behaviors of D-gun sprayed TBCs with a hollow spherical ZrO2-8y(2)O(3) (HSP-YSZ) top coat and NiCrAlY bond coat on directionally solidified Ni-base superalloys DZ125 were investigated at high temperature (1100 degrees C) <-> room temperature (RT) repeatedly by water quenching. Scanning electron microscopy (SEM) was used to characterize the coating microstructure and failure morphology. The results showed that failure of the D-gun sprayed TBC starts with crack initiation along the splats boundary in the ceramic top coat and the non-alumina oxides. The cracks propagate and coalesce with the increasing thermal cycling. The extensive cracking of the rapidly formed non-alumina oxides, resulting from the depletion of aluminum in the bond coat, aids to delamination of the outer ceramic layer. The stress distributions in TGO layer at different thermal shock cycles was measured by luminescence spectroscopy to investigate the failure mechanism of TBC system. (c) 2006 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/34284] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | P. L. Ke,Q. M. Wang,J. Gong,et al. Progressive damage during thermal shock cycling of D-gun sprayed thermal barrier coatings with hollow spherical ZrO2-8Y(2)O(3)[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2006,435:228-236. |
APA | P. L. Ke,Q. M. Wang,J. Gong,C. Sun,&Y. C. Zhou.(2006).Progressive damage during thermal shock cycling of D-gun sprayed thermal barrier coatings with hollow spherical ZrO2-8Y(2)O(3).Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,435,228-236. |
MLA | P. L. Ke,et al."Progressive damage during thermal shock cycling of D-gun sprayed thermal barrier coatings with hollow spherical ZrO2-8Y(2)O(3)".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 435(2006):228-236. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论