The oxidation behavior of Ti-46.5Al-5Nb at 900 degrees C | |
W. Lu ; C. L. Chen ; Y. J. Xi ; F. H. Wang ; L. L. He | |
刊名 | Intermetallics |
2007 | |
卷号 | 15期号:8页码:989-998 |
关键词 | titanium aluminides based on TiAl oxidation electron microscopy transmission gamma-titanium aluminides high-temperature air intermetallic alloys ternary-system tial alloys tem phase microstructure kappa-al2o3 diffraction |
ISSN号 | 0966-9795 |
中文摘要 | The early stages of Ti-46.5Al-5Nb (at%) oxidation at 900 degrees C have been investigated combined with TEM and STEM. The results reveal that a layer composed of polycrystalline TiO2 and amorphous Al2O3 phase formed firstly after 5-min oxidation. The base alloy connected with the oxide scale has some deformation compared with the inner full lamellar TiAl structure. After 30-min oxidation, the phases of gamma-Al2O3, kappa-Al2O3, titanium nitrides and Ti5Al3O2 were formed in the area from the nitride layer to base alloy. After 50 h of oxidation, Ti5Al3O2 vanishes at the interface of oxide scale/base alloy in Ti-46.5Al-5Nb, contrary to the continuous formation of Ti5Al3O2 in gamma-TiAl at the interface of oxide scale[base alloy, Al3Nb phase formed in this zone, which hinders the continuous formation of Ti5Al3O2. (C)2007 Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/33743] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | W. Lu,C. L. Chen,Y. J. Xi,et al. The oxidation behavior of Ti-46.5Al-5Nb at 900 degrees C[J]. Intermetallics,2007,15(8):989-998. |
APA | W. Lu,C. L. Chen,Y. J. Xi,F. H. Wang,&L. L. He.(2007).The oxidation behavior of Ti-46.5Al-5Nb at 900 degrees C.Intermetallics,15(8),989-998. |
MLA | W. Lu,et al."The oxidation behavior of Ti-46.5Al-5Nb at 900 degrees C".Intermetallics 15.8(2007):989-998. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论