Mechanical and environmental influences on stress corrosion cracking of an X-70 pipeline steel in dilute near-neutral pH solutions | |
B. Fang ; E. H. Han ; J. Wang ; W. Ke | |
刊名 | Corrosion |
2007 | |
卷号 | 63期号:5页码:419-432 |
关键词 | near-neutral pH pipeline steel potential slow strain rate test strain rate stress corrosion cracking strain-rate fatigue growth prediction initiation water x-80 |
ISSN号 | 0010-9312 |
中文摘要 | Slow strain rate tests (SSRT) were used to investigate stress corrosion cracking (SCC behavior of an X-70 pipeline steel in a soil solution and NS-4 solution, both saturated with 5% carbon dioxide (CO(2))/balance N(2) gas mixture at different potentials and strain rates. It was found that transgranular SCC occurred in this steel in the two solutions. The influence of strain rate was correlated with electrochemical potential. At a high strain rate, there were fewer cracks visible on the specimen side surface, but SCC occurred at a high cathodic protection potential. At a low strain rate, SCC susceptibility increased with decreasing an electrochemical potential. The SCC susceptibility was influenced greater in the soil solution than in the NS-4 solution. The susceptible local strain rate for near-neutral pH SCC was determined, which was lower than 5 x 10(-5) /s. There were several potential crack initiation sites including corrosion pits, inclusions, and flow lines formed during the rolling process of the steel. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/33520] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | B. Fang,E. H. Han,J. Wang,et al. Mechanical and environmental influences on stress corrosion cracking of an X-70 pipeline steel in dilute near-neutral pH solutions[J]. Corrosion,2007,63(5):419-432. |
APA | B. Fang,E. H. Han,J. Wang,&W. Ke.(2007).Mechanical and environmental influences on stress corrosion cracking of an X-70 pipeline steel in dilute near-neutral pH solutions.Corrosion,63(5),419-432. |
MLA | B. Fang,et al."Mechanical and environmental influences on stress corrosion cracking of an X-70 pipeline steel in dilute near-neutral pH solutions".Corrosion 63.5(2007):419-432. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论