Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature

CORC > 金属研究所 > 中国科学院金属研究所

	Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature
	Y. M. Xiong ; S. L. Zhu ; F. H. Wang
刊名	Corrosion Science
	2008
卷号	50 期号:1 页码:15-22
关键词	titanium metal coatings X-ray diffraction high temperature corrosion oxide coatings alumina scale formation oxide hydroxide evaporation al-cr alloys oxidation behavior water-vapor titanium aluminides cyclic oxidation coatings chromium intermetallics
ISSN号	0010-938X
中文摘要	In the present paper, the corrosion behavior of Ti60 alloys with an aluminide, TiAlCr, and enamel coatings in moist air containing NaCl vapor at 700-800 degrees C were studied. The results showed that the TiAlCr and aluminide coatings failed to protect the substrate from corrosion due to the cyclic formation of volatile products during corrosion at 800 degrees C. However, an uneven continuous protective Al2O3 scale could form on the aluminide coating during corrosion at 700 degrees C. And the enamel coating could protect Ti60 from corrosion due to its high thermochernical stability and matched thermal expansion coefficient with substrates of Ti-base alloys during corrosion. (c) 2007 Elsevier Ltd. All rights reserved.
原文出处	://WOS:000253093100004
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://210.72.142.130/handle/321006/33238]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. M. Xiong,S. L. Zhu,F. H. Wang. Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature[J]. Corrosion Science,2008,50(1):15-22.
APA	Y. M. Xiong,S. L. Zhu,&F. H. Wang.(2008).Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature.Corrosion Science,50(1),15-22.
MLA	Y. M. Xiong,et al."Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature".Corrosion Science 50.1(2008):15-22.