On the formation of GBF of high-strength steels in the very high cycle fatigue regime | |
Y. B. Liu ; Z. G. Yang ; Y. D. Li ; S. M. Chen ; S. X. Li ; W. J. Hui ; Y. Q. Weng | |
刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
![]() |
2008 | |
卷号 | 497期号:1-2页码:408-415 |
关键词 | Very high cycle fatigue High-strength steels GBF Stress intensity factor Hydrogen chromium-bearing steel long-life fatigue crack initiation inclusion size hydrogen behavior failure growth mechanism fracture |
ISSN号 | 0921-5093 |
中文摘要 | Very high cycle fatigue tests were conducted for six high-strength steels by using a 20-kHz ultrasonic fatigue testing machine. Most tests were conducted on one stress amplitude until 109 cycles: however, for further examination of the formation of the granular-bright-facet (GBF) on the fracture surface, a two-step loading test for commercial 60Si2Mn specimens was adopted. The failure of almost all specimens is caused by internal non-metallic inclusion. Experimental results show that the stress intensity factor at the edge of GBF on the fracture surface, K(GBF), is not a constant but proportional to (root area(GBF))(1/3). It means that KGBF does not correspond to the threshold value of a long crack but the threshold value of a small crack. The stress intensity factor, k(H), caused by hydrogen plays an important role during formation of GBF. (C) 2008 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/32980] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. B. Liu,Z. G. Yang,Y. D. Li,et al. On the formation of GBF of high-strength steels in the very high cycle fatigue regime[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2008,497(1-2):408-415. |
APA | Y. B. Liu.,Z. G. Yang.,Y. D. Li.,S. M. Chen.,S. X. Li.,...&Y. Q. Weng.(2008).On the formation of GBF of high-strength steels in the very high cycle fatigue regime.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,497(1-2),408-415. |
MLA | Y. B. Liu,et al."On the formation of GBF of high-strength steels in the very high cycle fatigue regime".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 497.1-2(2008):408-415. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论