Study on fatigue property of a new 2.8 GPa grade maraging steel | |
W. Wang ; W. Yan ; Q. Q. Duan ; Y. Y. Shan ; Z. F. Zhang ; K. Yang | |
刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing |
2010 | |
卷号 | 527期号:13-14页码:3057-3063 |
关键词 | Maraging steel Fatigue property S-N curve Fatigue crack high-strength steel part i failure mechanism hydrogen behavior phase |
ISSN号 | 0921-5093 |
中文摘要 | A new 2.8 GPa grade maraging steel was developed in the present work and the tension-tension fatigue property of the steel was studied after peak-aging treatment. The results showed that the steel could reach an ultimate tensile strength of 2760 MPa, a fracture toughness of 31.6 MPa m(1/2), and a fatigue limit of 1150 MPa at stress ratio of 0.1. It was revealed that the fatigue crack initiation of the steel mainly originated from the surface at high stress level but from the interior inclusions at low stress level. From the observations by transmission electron microscope (TEM) and fatigue crack propagation curves, it was proposed that the cyclic softening occurred, which was induced by the resolution as well as the growth of precipitates, and the poor fatigue crack growth resistance and high fatigue crack propagation rate might be the main reason for the relatively low fatigue limit of the steel. (C) 2010 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/31519] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | W. Wang,W. Yan,Q. Q. Duan,et al. Study on fatigue property of a new 2.8 GPa grade maraging steel[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2010,527(13-14):3057-3063. |
APA | W. Wang,W. Yan,Q. Q. Duan,Y. Y. Shan,Z. F. Zhang,&K. Yang.(2010).Study on fatigue property of a new 2.8 GPa grade maraging steel.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,527(13-14),3057-3063. |
MLA | W. Wang,et al."Study on fatigue property of a new 2.8 GPa grade maraging steel".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 527.13-14(2010):3057-3063. |