Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2 | |
F. Z. Wang ; Q. Z. Wang ; B. H. Yu ; B. L. Xiao ; Z. Y. Ma | |
刊名 | Journal of Materials Processing Technology |
2011 | |
卷号 | 211期号:11页码:1804-1809 |
关键词 | Brazing Ti(C N)-based cermet Steel Microstructure Mechanical properties isothermal solidification |
ISSN号 | 0924-0136 |
中文摘要 | The effects of brazing temperature on microstructure and bonding strength of vacuum brazed joints of Ti(C,N)-based cermet and 17-4 PH stainless steel, using filler metal BNi-2, were investigated. At a lower brazing temperature of 1050 C. the distribution of melting point depressants (MPD) concentrated on the diffusion affected zone (DAZ) and the brazing seam near the Ti(C,N)-based cermet, the generation of brittle phases in the brazing seam was unavoidable. The uniform distribution of the MPD and full solid solution of gamma-nickel occurred in the brazing seam at a higher brazing temperature of 1150 degrees C. A maximum shear strength of 690 MPa was achieved at a brazing temperature of 1150 degrees C. (C) 2011 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/30717] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | F. Z. Wang,Q. Z. Wang,B. H. Yu,et al. Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2[J]. Journal of Materials Processing Technology,2011,211(11):1804-1809. |
APA | F. Z. Wang,Q. Z. Wang,B. H. Yu,B. L. Xiao,&Z. Y. Ma.(2011).Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2.Journal of Materials Processing Technology,211(11),1804-1809. |
MLA | F. Z. Wang,et al."Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2".Journal of Materials Processing Technology 211.11(2011):1804-1809. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论