Oxidation behavior and effect of oxidation on tensile properties of Ti60 alloy | |
W. J. Jia ; W. D. Zeng ; X. M. Zhang ; Y. G. Zhou ; J. R. Liu ; Q. J. Wang | |
刊名 | Journal of Materials Science
![]() |
2011 | |
卷号 | 46期号:5页码:1351-1358 |
关键词 | high-temperature oxidation titanium-alloys ti-6al-4v alloy improvement resistance surface microstructure coatings ti-1100 |
ISSN号 | 0022-2461 |
中文摘要 | Oxidation behavior of a near-alpha Ti60 titanium alloy was investigated in the temperature range of 600-750 A degrees C for up to 100 h exposure. The results showed that the oxidation kinetics of Ti60 alloy followed parabolic kinetics below 700 A degrees C but parabolic-linear kinetics above 700 A degrees C. The total activation energy was calculated to be 256 kJ/mol over the whole temperature range. The oxidation products were TiO(2) after thermal exposure at 700 A degrees C for 100 h, but a mixture of TiO(2) and a small amount of Al(2)O(3) for the specimens oxidized at 750 A degrees C for 50 h. The grain boundaries were preferred sites for oxidation products formation during the oxidation. The tensile tests were performed at room temperature for specimens before and after oxidation. Both of the strength and ductility decreased for the specimens with oxide scale. However, both of them increased when the oxide scale was removed before testing. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/30418] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | W. J. Jia,W. D. Zeng,X. M. Zhang,et al. Oxidation behavior and effect of oxidation on tensile properties of Ti60 alloy[J]. Journal of Materials Science,2011,46(5):1351-1358. |
APA | W. J. Jia,W. D. Zeng,X. M. Zhang,Y. G. Zhou,J. R. Liu,&Q. J. Wang.(2011).Oxidation behavior and effect of oxidation on tensile properties of Ti60 alloy.Journal of Materials Science,46(5),1351-1358. |
MLA | W. J. Jia,et al."Oxidation behavior and effect of oxidation on tensile properties of Ti60 alloy".Journal of Materials Science 46.5(2011):1351-1358. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论