Correlative characterization on microstructure evolution of Ni-based K403 alloy during thermal exposure | |
Liu, Jun; Li, Jiehua; Hage, Fredrik S.; Ghosh, Pradipta; Li, Jun; Wang, Wei; Chen, Zongning; Wang, Tongmin; Tang, Wenting; Ramasse, Quentin | |
刊名 | ACTA MATERIALIA |
2017 | |
卷号 | 131页码:169-186 |
关键词 | K403 Ni based superalloy Thermal exposure Carbide Topologically close-packed phase HAADF-STEM EELS |
ISSN号 | 1359-6454 |
URL标识 | 查看原文 |
WOS记录号 | [DB:DC_IDENTIFIER_WOSID] |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/3283918 |
专题 | 大连理工大学 |
作者单位 | 1.Xian Univ Technol, Sch Mat Sci & Engn, Xian 710048, Peoples R China. 2.Univ Leoben, Inst Casting Res, A-8700 Leoben, Austria. 3.SuperSTEM Lab, SciTech Daresbury Campus,Keckwick Lane, Warrington WA4 4AD, Cheshire, England. 4.Austrian Acad Sci, Erich Schmid Inst Mat Sci, A-8700 Leoben, Austria. 5.Shanghai Jiao Tong Univ, Dept Mat Sci & Engn, Shanghai 200240, Peoples R China. 6.Dalian Univ Technol, Sch Mat Sci & Engn, Key Lab Solidificat Control & Digital Preparat Te, Dalian 116024, Peoples R China. 7.Univ Leoben, Inst Casting Res, A-8700 Leoben, Austria. 8.Austrian Foundry Res Inst, Leoben, Austria. |
推荐引用方式 GB/T 7714 | Liu, Jun,Li, Jiehua,Hage, Fredrik S.,et al. Correlative characterization on microstructure evolution of Ni-based K403 alloy during thermal exposure[J]. ACTA MATERIALIA,2017,131:169-186. |
APA | Liu, Jun.,Li, Jiehua.,Hage, Fredrik S..,Ghosh, Pradipta.,Li, Jun.,...&Schumacher, Peter.(2017).Correlative characterization on microstructure evolution of Ni-based K403 alloy during thermal exposure.ACTA MATERIALIA,131,169-186. |
MLA | Liu, Jun,et al."Correlative characterization on microstructure evolution of Ni-based K403 alloy during thermal exposure".ACTA MATERIALIA 131(2017):169-186. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论