A twin orientation relationship between {001} and {111} obtained in Ta-2.5W alloy during heavily cold rolling | |
Wang, S.; Feng, S. K.; Chen, C.; Jia, Y. L.; Wang, M. P.; Li, Z.; Zhong, Z. H.; Lu, P.; Li, P.; Cao, L. F. | |
刊名 | MATERIALS CHARACTERIZATION |
2017 | |
卷号 | 125页码:108-113 |
关键词 | Shear bands {001} < 210 > orientation Microbands Deformation mechanism Ta-W alloy |
ISSN号 | 1044-5803 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2946652 |
专题 | 西安交通大学 |
推荐引用方式 GB/T 7714 | Wang, S.,Feng, S. K.,Chen, C.,et al. A twin orientation relationship between {001} and {111} obtained in Ta-2.5W alloy during heavily cold rolling[J]. MATERIALS CHARACTERIZATION,2017,125:108-113. |
APA | Wang, S..,Feng, S. K..,Chen, C..,Jia, Y. L..,Wang, M. P..,...&Wu, Y. C..(2017).A twin orientation relationship between {001} and {111} obtained in Ta-2.5W alloy during heavily cold rolling.MATERIALS CHARACTERIZATION,125,108-113. |
MLA | Wang, S.,et al."A twin orientation relationship between {001} and {111} obtained in Ta-2.5W alloy during heavily cold rolling".MATERIALS CHARACTERIZATION 125(2017):108-113. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论