| Corrosion fatigue crack propagation behavior of S135 high-strength drill pipe steel in H2S environment | |
| Liu, Ming; Luo, Sheji; Shen, Yi; Lin, Xiuzhou | |
| 刊名 | ENGINEERING FAILURE ANALYSIS
 |
| 2019 | |
| 卷号 | 97页码:493-505 |
| 关键词 | Corrosion fatigue Drill pipe steel Elastic fracture mechanics Hydrogen sulfide |
| ISSN号 | 1350-6307 |
| URL标识 | 查看原文 |
| 内容类型 | 期刊论文 |
| URI标识 | http://www.corc.org.cn/handle/1471x/2827284 |
| 专题 | 西安交通大学 |
| 推荐引用方式 GB/T 7714 | Liu, Ming,Luo, Sheji,Shen, Yi,et al. Corrosion fatigue crack propagation behavior of S135 high-strength drill pipe steel in H2S environment[J]. ENGINEERING FAILURE ANALYSIS,2019,97:493-505. |
| APA | Liu, Ming,Luo, Sheji,Shen, Yi,&Lin, Xiuzhou.(2019).Corrosion fatigue crack propagation behavior of S135 high-strength drill pipe steel in H2S environment.ENGINEERING FAILURE ANALYSIS,97,493-505. |
| MLA | Liu, Ming,et al."Corrosion fatigue crack propagation behavior of S135 high-strength drill pipe steel in H2S environment".ENGINEERING FAILURE ANALYSIS 97(2019):493-505. |