Thermal Shock Resistance of Chemical Vapour Deposited Zinc Sulfide at   Elevated Temperatures

doi:10.1080/0371750X.2016.1210026

CORC > 北京大学 > 工学院

	Thermal Shock Resistance of Chemical Vapour Deposited Zinc Sulfide at Elevated Temperatures
	Cheng, Tianbao ; Li, Weiguo ; Qu, Zhaoliang ; Wen, Weibin ; Fang, Daining
刊名	TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY
	2016
关键词	Thermal shock resistance Zinc sulfide Temperature dependent material properties Compressive strength effect Convective cooling OPTICAL-MATERIALS CERAMICS ZNS ENVIRONMENTS EXPANSION STRENGTH
DOI	10.1080/0371750X.2016.1210026
英文摘要	For traditional bulk ceramics, the compressive strength is much greater than the tensile strength. Thus, only the tensile failure is usually considered in the thermal shock resistance (TSR) of these ceramics. However, the compressive strength of chemical vapour deposited (CVD) zinc sulfide (ZnS) is relatively low. It thus becomes critical in evaluating the TSR of CVD ZnS at elevated temperatures. In the present work, the compressive and tensile strengths are measured from room temperature to 600 degrees C and then the TSR of CVD ZnS is studied. It is found that the TSR of CVD ZnS under aerodynamic thermal environments will be over-estimated significantly if the compressive strength is neglected. The study also shows the importance of considering the temperature dependence of the material properties to evaluate the TSR of CVD ZnS. Moreover, convective cooling can improve the TSR of CVD ZnS caused by aerodynamic heating at the upper surface. However, it can also lead to thermal down shock at the lower surface. To ensure that convective cooling will not cause the fracture of CVD ZnS, heat transfer condition should be less than the corresponding critical heat transfer condition.; Chongqing Graduate Student Research Innovation Project [CYB14030]; National Natural Science Foundation of China [11102003, 11227801, 91216301, 11172336, 11472066]; Program for New Century Excellent Talents in University [ncet-13-0634]; Chongqing Natural Science Foundation [cstc2013jcyjA50018]; SCI(E); ARTICLE; wgli@cqu.edu.cn; 4; 215-219; 75
语种	英语
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/459048]
专题	工学院
推荐引用方式 GB/T 7714	Cheng, Tianbao,Li, Weiguo,Qu, Zhaoliang,et al. Thermal Shock Resistance of Chemical Vapour Deposited Zinc Sulfide at Elevated Temperatures[J]. TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY,2016.
APA	Cheng, Tianbao,Li, Weiguo,Qu, Zhaoliang,Wen, Weibin,&Fang, Daining.(2016).Thermal Shock Resistance of Chemical Vapour Deposited Zinc Sulfide at Elevated Temperatures.TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY.
MLA	Cheng, Tianbao,et al."Thermal Shock Resistance of Chemical Vapour Deposited Zinc Sulfide at Elevated Temperatures".TRANSACTIONS OF THE INDIAN CERAMIC SOCIETY (2016).