	Cheng, Tianbao ; Li, Weiguo ; Li, Qingming ; Kou, Haibo ; Fang, Daining
	2014
关键词	High-temperature testing three-point bending strength temperature-dependent material properties polycrystalline alumina brittle-ductile transition microstructure sensitivity THERMAL-SHOCK RESISTANCE HIGH-PURITY ALUMINA ELEVATED-TEMPERATURES REFRACTORY MATERIALS ZIRCONIUM DIBORIDE SAPPHIRE WHISKERS BRITTLE FRACTURE SINGLE CRYSTAL YOUNG MODULUS CERAMICS
英文摘要	The knowledge of the fracture strength of solids from room temperature to melting point is not only important for practical application but also useful for the understanding of the failure mechanisms of materials at elevated temperatures. In the present work, an apparatus for high-temperature mechanical testing has been developed and described in detail. The load-displacement curves of the bulk polycrystalline alumina from room temperature to melting point are measured on a three-point bending configuration. The bending strength is calculated from the updated formula of material mechanics which includes the temperature-dependent thermal expansions of the fixture and specimen. The brittle-ductile transition temperature of polycrystalline alumina is identified and is similar to 1500 degrees C. The strength-temperature curves below and above brittle-ductile transition temperature are convex and concave, respectively. Strength is sensitive to defects at lower temperatures. Not only the values also the temperature dependence of the strength are affected by impurity and microflaws significantly. This is different from Young's modulus whose temperature dependence is insensitive to microstructure of materials.; Thermodynamics; Mechanics; Materials Science, Characterization & Testing; SCI(E); EI; 0; ARTICLE; wgli@cqu.edu.cn; 4; 285-295; 43
语种	英语
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/390574]
专题	工学院
推荐引用方式 GB/T 7714	Cheng, Tianbao,Li, Weiguo,Li, Qingming,et al. The bending strength of bulk polycrystalline alumina from room temperature to melting point[J],2014.
APA	Cheng, Tianbao,Li, Weiguo,Li, Qingming,Kou, Haibo,&Fang, Daining.(2014).The bending strength of bulk polycrystalline alumina from room temperature to melting point..
MLA	Cheng, Tianbao,et al."The bending strength of bulk polycrystalline alumina from room temperature to melting point".(2014).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。