Effect of Aging Treatment on Superelasticity of a Ti48.8Ni50.8V0.4 Alloy | |
Zhao, H. ; Liang, C. Q. ; Liu, J. T. ; Tong, Y. X. ; Chen, F. ; Tian, B. ; Li, L. ; Zheng, Y. F. | |
2012 | |
关键词 | mechanical property microstructure shape memory alloy superelasticity TiNiV SHAPE-MEMORY ALLOYS TI-50.9 AT.PERCENT NI TRANSFORMATION BEHAVIOR MARTENSITIC-TRANSFORMATION DEFORMATION-BEHAVIOR |
DOI | 10.1007/s11665-012-0373-2 |
英文摘要 | In this study, effect of aging treatment on microstructure, deformation behavior, and superelasticity of Ti48.8Ni50.8V0.4 alloy was investigated. After aging at 400 A degrees C for 30 min, Ti3Ni4 precipitates formed. With increasing aging temperature from 300 to 450 A degrees C, the yield strength of reoriented martensite increased due to the strengthening effect of Ti3Ni4 phase, thus improved the shape recovery ratio and reduced the stress hysteresis. Further increasing the aging temperature, the size of Ti3Ni4 precipitates increased and the coherency between precipitate and matrix gradually lost, leading to the decreasing yield strength of reoriented martensite and shape recovery ratio. Simultaneously, the stress hysteresis increased resulting from the hinder of plastic deformation to the interfacial movement during phase transformation. The critical stress to induce martensitic transformation continuously decreased with increasing aging temperature.; Materials Science, Multidisciplinary; SCI(E); EI; CPCI-S(ISTP); 3 |
语种 | 英语 |
内容类型 | 会议论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/229022] |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Zhao, H.,Liang, C. Q.,Liu, J. T.,et al. Effect of Aging Treatment on Superelasticity of a Ti48.8Ni50.8V0.4 Alloy[C]. 见:. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论