Processable PMR poly(pyrrolone-imide)s matrix resins and their short carbon fiber-reinforced composites

doi:10.1177/0954008304038054

CORC > 化学研究所 > 中国科学院化学研究所

	Processable PMR poly(pyrrolone-imide)s matrix resins and their short carbon fiber-reinforced composites
	Shang, YM ; Fan, L ; Gao, SQ ; Hu, AJ ; Yang, SY
刊名	HIGH PERFORMANCE POLYMERS
	2004-03-01
卷号	16 期号:1 页码:39-54
关键词	Poly(Pyrrolone-imide)s Pmr Polymer Composites Short Carbon Fiber
ISSN号	0954-0083
DOI	10.1177/0954008304038054
英文摘要	Processable poly(pyrrolone-imide)s (PPI) were prepared via PMR process from diethyl ester of 4,4'-(hexafluoroisopropylidene)diphthalic acid (6FDE), 3,3',4,4'-tetraaminodiphenyl ether (TADPE), p phenylenediamine (p-PDA) and monoethyl ester of cis-5-norbomene-endo-2,3-dicarboxylic acid (NE) using methyl alcohol as solvent. The homogenous PPI matrix resin solutions with 32 wt.% solid content had the low absolute viscosities in the range of 80-90 mPa s at 25 degreesC. The matrix resin solutions were stable for a period of > 2 months at the refrigerator temperature (4 degreesC) and showed good adhesion on carbon fibers. The matrix resin solutions could be thermally converted to B-stage end-capped prepolymer, which was then thermally processed to yield the fully-cured PPI. Experimental results demonstrated that the fully-cured PPI exhibited good thermal stability with glass transition temperatures of > 400 degreesC and the thermal decomposition temperature of 525-537 degreesC. The onset temperatures of the DMA storage modulus curve for PPI-20 was as high as 395 degreesC and the storage modulus retention was 71% at 370 degreesC. The short carbon fiber-reinforced PPI composites (CF/PPI) were also fabricated. The CF/PPI composites showed excellent thermal stabilities and good mechanical properties, with glass transition temperature in the range of 413-421 degreesC and the storage modulus retention of 76-87% at 370 degreesC.
语种	英语
出版者	SAGE PUBLICATIONS LTD
WOS记录号	WOS:000220178900003
内容类型	期刊论文
源URL	[http://ir.iccas.ac.cn/handle/121111/82287]
专题	中国科学院化学研究所
通讯作者	Yang, SY
作者单位	1.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, State Key Lab Engn Plast, Beijing 100080, Peoples R China 2.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Adv Polymer Mat Lab, Beijing 100080, Peoples R China
推荐引用方式 GB/T 7714	Shang, YM,Fan, L,Gao, SQ,et al. Processable PMR poly(pyrrolone-imide)s matrix resins and their short carbon fiber-reinforced composites[J]. HIGH PERFORMANCE POLYMERS,2004,16(1):39-54.
APA	Shang, YM,Fan, L,Gao, SQ,Hu, AJ,&Yang, SY.(2004).Processable PMR poly(pyrrolone-imide)s matrix resins and their short carbon fiber-reinforced composites.HIGH PERFORMANCE POLYMERS,16(1),39-54.
MLA	Shang, YM,et al."Processable PMR poly(pyrrolone-imide)s matrix resins and their short carbon fiber-reinforced composites".HIGH PERFORMANCE POLYMERS 16.1(2004):39-54.