Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers | |
Mochizuki, M; Nakayama, K; Qian, RY; Jiang, BZ; Hirami, M; Hayashi, T; Masuda, T; Nakajima, A | |
刊名 | PURE AND APPLIED CHEMISTRY |
1997-12-01 | |
卷号 | 69期号:12页码:2567-2575 |
ISSN号 | 0033-4545 |
英文摘要 | Using high molecular weight (M-n=80,000) Poly(hexano-6-lactone) (PCL'), tough and high tenacity PCL monofilaments with various draw ratios (undrawn to 9 times drawn) were prepared by melt-spinning. The relationship between microstructure and properties of the PCL fibers is described in this current IUPAC Technical Report. Analysis of microstructure of the drawn PCL fibers by wide-angle X-ray diffraction revealed typical c-axis orientation with an increase in crystallinity. It was also supported by sonic velocity measurements. The thermal, mechanical, and dynamic mechanical properties of the PCL fibers were affected significantly by draw ratio. DSC thermograms showed that the melting temperature and the enthalpy of fusion increased with draw ratio. The temperature dependence curves of dynamic viscoelasticity showed that the temperature at tan delta peak of alpha dispersion corresponding to the glass transition temperature shifted toward higher temperature and the peak value of tan delta decreased with draw ratio. The dynamic storage modulus and the sonic modulus increased with draw ratio. These results are due to the increase in crystallinity and molecular orientation with drawing, and are responsible for an increase in tensile tenacity as well as knot tenacity of the PCL fibers. |
语种 | 英语 |
出版者 | BLACKWELL SCIENCE LTD |
WOS记录号 | WOS:000071217300008 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/74109] |
专题 | 中国科学院化学研究所 |
通讯作者 | Mochizuki, M |
作者单位 | 1.Unitika Ltd, Ctr Res & Dev, Uji, Kyoto 611, Japan 2.Natl Inst Mat & Chem Res, Tsukuba, Ibaraki 305, Japan 3.Acad Sinica, Inst Chem, Beijing 100080, Peoples R China 4.Acad Sinica, Changchun Inst Appl Chem, Changchun 130022, Jilin, Peoples R China 5.Univ Osaka Prefecture, Adv Sci & Technol Res Inst, Sakai, Osaka 593, Japan 6.Kyoto Univ, Dept Chem Mat, Sakyo Ku, Kyoto 60601, Japan |
推荐引用方式 GB/T 7714 | Mochizuki, M,Nakayama, K,Qian, RY,et al. Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers[J]. PURE AND APPLIED CHEMISTRY,1997,69(12):2567-2575. |
APA | Mochizuki, M.,Nakayama, K.,Qian, RY.,Jiang, BZ.,Hirami, M.,...&Nakajima, A.(1997).Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers.PURE AND APPLIED CHEMISTRY,69(12),2567-2575. |
MLA | Mochizuki, M,et al."Studies on biodegradable poly(hexano-6-lactone) fibers 1. Structure and properties of drawn poly(hexano-6-lactone) fibers".PURE AND APPLIED CHEMISTRY 69.12(1997):2567-2575. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论