Reduced hot cracking susceptibility by controlling the fusion ratio in laser welding of dissimilar Al alloys joints | |
Zhang, Yulong[1]; Lu, Fenggui[2]; Wang, Hui-Ping[3]; Wang, Xiaojie[4]; Cui, Haichao[5]; Tang, Xinhua[6] | |
刊名 | JOURNAL OF MATERIALS RESEARCH |
2015 | |
卷号 | 30页码:993-1001 |
ISSN号 | 0884-2914 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2237190 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China. 2.[2]Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China. 3.Shanghai Univ, Shanghai Key Lab Modern Met & Mat Proc, Shanghai 200072, Peoples R China. 4.[3]Gen Motors Global Res & Dev, Mfg Syst Res Lab, Warren, MI 48090 USA. 5.[4]Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China. 6.[5]Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China. 7.[6]Shanghai Jiao Tong Univ, Shanghai Key Lab Mat Laser Proc & Modificat, Shanghai 200240, Peoples R China. |
推荐引用方式 GB/T 7714 | Zhang, Yulong[1],Lu, Fenggui[2],Wang, Hui-Ping[3],et al. Reduced hot cracking susceptibility by controlling the fusion ratio in laser welding of dissimilar Al alloys joints[J]. JOURNAL OF MATERIALS RESEARCH,2015,30:993-1001. |
APA | Zhang, Yulong[1],Lu, Fenggui[2],Wang, Hui-Ping[3],Wang, Xiaojie[4],Cui, Haichao[5],&Tang, Xinhua[6].(2015).Reduced hot cracking susceptibility by controlling the fusion ratio in laser welding of dissimilar Al alloys joints.JOURNAL OF MATERIALS RESEARCH,30,993-1001. |
MLA | Zhang, Yulong[1],et al."Reduced hot cracking susceptibility by controlling the fusion ratio in laser welding of dissimilar Al alloys joints".JOURNAL OF MATERIALS RESEARCH 30(2015):993-1001. |