Effect of work hardening on mechanical behavior of resistance spot welding joint during tension shear test | |
Liu, Chengjie[1]; Zheng, Xiankun[2]; He, Hongyu[3]; Wang, Wurong[4]; Wei, Xicheng[5] | |
刊名 | MATERIALS & DESIGN
![]() |
2016 | |
卷号 | 100页码:188-197 |
关键词 | Work hardening Resistance spot welding Mechanical behavior Fracture characteristic HAZ analysis |
ISSN号 | 0264-1275 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2236200 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, Sch Mat Sci & Engn, Shanghai, Peoples R China. 2.[2]Shanghai Univ, Sch Mat Sci & Engn, Shanghai, Peoples R China. 3.[3]Shanghai Univ, Sch Mat Sci & Engn, Shanghai, Peoples R China. 4.[4]Shanghai Univ, Sch Mat Sci & Engn, Shanghai, Peoples R China. 5.[5]Shanghai Univ, Sch Mat Sci & Engn, Shanghai, Peoples R China. |
推荐引用方式 GB/T 7714 | Liu, Chengjie[1],Zheng, Xiankun[2],He, Hongyu[3],et al. Effect of work hardening on mechanical behavior of resistance spot welding joint during tension shear test[J]. MATERIALS & DESIGN,2016,100:188-197. |
APA | Liu, Chengjie[1],Zheng, Xiankun[2],He, Hongyu[3],Wang, Wurong[4],&Wei, Xicheng[5].(2016).Effect of work hardening on mechanical behavior of resistance spot welding joint during tension shear test.MATERIALS & DESIGN,100,188-197. |
MLA | Liu, Chengjie[1],et al."Effect of work hardening on mechanical behavior of resistance spot welding joint during tension shear test".MATERIALS & DESIGN 100(2016):188-197. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论