	The role of Ti and Si in the nucleation of alpha-Al during hot dip coating of steel with Al-43.4 wt.%Zn-1.6 wt.%Si alloy
	Peng, Wangjun[1]; Du, Qing[2]; Wu, Guangxin[3]; Dan, Wende[4]; Hu, Weidong[5]; Zhang, Jieyu[6]
刊名	SURFACE & COATINGS TECHNOLOGY
	2016
卷号	299页码:56-64
关键词	TiAl3 Al-43.4 wt.%Zn-1.6 wt.%Si Lattice coherence Interface bonding energy
ISSN号	0257-8972
URL标识	查看原文
内容类型	期刊论文
URI标识	http://www.corc.org.cn/handle/1471x/2232826
专题	上海大学
作者单位	1.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 2.Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China. 3.Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China.
推荐引用方式 GB/T 7714	Peng, Wangjun[1],Du, Qing[2],Wu, Guangxin[3],et al. The role of Ti and Si in the nucleation of alpha-Al during hot dip coating of steel with Al-43.4 wt.%Zn-1.6 wt.%Si alloy[J]. SURFACE & COATINGS TECHNOLOGY,2016,299:56-64.
APA	Peng, Wangjun[1],Du, Qing[2],Wu, Guangxin[3],Dan, Wende[4],Hu, Weidong[5],&Zhang, Jieyu[6].(2016).The role of Ti and Si in the nucleation of alpha-Al during hot dip coating of steel with Al-43.4 wt.%Zn-1.6 wt.%Si alloy.SURFACE & COATINGS TECHNOLOGY,299,56-64.
MLA	Peng, Wangjun[1],et al."The role of Ti and Si in the nucleation of alpha-Al during hot dip coating of steel with Al-43.4 wt.%Zn-1.6 wt.%Si alloy".SURFACE & COATINGS TECHNOLOGY 299(2016):56-64.

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。