The effect of Al-5 wt%Ti-0.2 wt%B on the solidification characteristics of 55 wt%Al-Zn-1.6 wt%Si alloy in hot-dip coating | |
Peng, Wangjun[1]; Wu, Guangxin[2]; Peng, Hao[3]; Ding, Dejian[4]; Yu, Yaowei[5]; Zhang, Jieyu[6] | |
刊名 | SURFACE & COATINGS TECHNOLOGY |
2016 | |
卷号 | 306页码:378-389 |
关键词 | Thermal analysis 55 wt%Al-Zn-1.6 wt%Si alloy Al-5 wt%Ti-0.2 wt%B Fourier method Latent heat |
ISSN号 | 0257-8972 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2227601 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 2.[2]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 3.[3]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 4.[4]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 5.[5]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 6.[6]Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. |
推荐引用方式 GB/T 7714 | Peng, Wangjun[1],Wu, Guangxin[2],Peng, Hao[3],et al. The effect of Al-5 wt%Ti-0.2 wt%B on the solidification characteristics of 55 wt%Al-Zn-1.6 wt%Si alloy in hot-dip coating[J]. SURFACE & COATINGS TECHNOLOGY,2016,306:378-389. |
APA | Peng, Wangjun[1],Wu, Guangxin[2],Peng, Hao[3],Ding, Dejian[4],Yu, Yaowei[5],&Zhang, Jieyu[6].(2016).The effect of Al-5 wt%Ti-0.2 wt%B on the solidification characteristics of 55 wt%Al-Zn-1.6 wt%Si alloy in hot-dip coating.SURFACE & COATINGS TECHNOLOGY,306,378-389. |
MLA | Peng, Wangjun[1],et al."The effect of Al-5 wt%Ti-0.2 wt%B on the solidification characteristics of 55 wt%Al-Zn-1.6 wt%Si alloy in hot-dip coating".SURFACE & COATINGS TECHNOLOGY 306(2016):378-389. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论