Steam oxidation resistance of plasma sprayed chromium-containing coatings at 1200 degrees C | |
Yang, Zhao[1]; Niu, Yaran[2]; Xue, Jiaxiang[3]; Liu, Tao[4]; Chang, Chengkang[5]; Zheng, Xuebin[6] | |
刊名 | MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION |
2019 | |
卷号 | 70页码:37-47 |
关键词 | air plasma spray Cr3C2-NiCr coating high-temperature steam oxidation NiCr coating Zircaloy claddings |
ISSN号 | 0947-5117 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2164401 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Inst Technol, Sch Mat Sci & Engn, Shanghai 200235, Peoples R China. 2.Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat CAS, Shanghai 200050, Peoples R China. 3.[2]Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat CAS, Shanghai 200050, Peoples R China. 4.[3]China Nucl Power Technol Res Inst, Shenzhen, Peoples R China. 5.[4]Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat CAS, Shanghai 200050, Peoples R China. 6.[5]Shanghai Inst Technol, Sch Mat Sci & Engn, Shanghai 200235, Peoples R China. 7.Shanghai Univ, Shanghai Innovat Inst Mat, Shanghai, Peoples R China. 8.[6]Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat CAS, Shanghai 200050, Peoples R China. |
推荐引用方式 GB/T 7714 | Yang, Zhao[1],Niu, Yaran[2],Xue, Jiaxiang[3],et al. Steam oxidation resistance of plasma sprayed chromium-containing coatings at 1200 degrees C[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2019,70:37-47. |
APA | Yang, Zhao[1],Niu, Yaran[2],Xue, Jiaxiang[3],Liu, Tao[4],Chang, Chengkang[5],&Zheng, Xuebin[6].(2019).Steam oxidation resistance of plasma sprayed chromium-containing coatings at 1200 degrees C.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,70,37-47. |
MLA | Yang, Zhao[1],et al."Steam oxidation resistance of plasma sprayed chromium-containing coatings at 1200 degrees C".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 70(2019):37-47. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论