Very High Cycle Fatigue Failure Mechanism of TC17 Alloy | |
Liu, HQ; He, C; Huang, ZY; Wang, QY | |
刊名 | ACTA METALLURGICA SINICA |
2017 | |
卷号 | Vol.53 No.9页码:1047-1054 |
关键词 | TC17 alloy very high cycle fatigue fatigue failure mechanism slip fracture |
ISSN号 | 0412-1961 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/1842379 |
专题 | 四川大学 |
作者单位 | 1.Chengdu Univ, Sch Architecture & Civil Engn, Chengdu 610106, Sichuan, Peoples R China 2.Sichuan Univ, Sch Aeronaut & Astronaut, Chengdu 610065, Sichuan, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, HQ,He, C,Huang, ZY,et al. Very High Cycle Fatigue Failure Mechanism of TC17 Alloy[J]. ACTA METALLURGICA SINICA,2017,Vol.53 No.9:1047-1054. |
APA | Liu, HQ,He, C,Huang, ZY,&Wang, QY.(2017).Very High Cycle Fatigue Failure Mechanism of TC17 Alloy.ACTA METALLURGICA SINICA,Vol.53 No.9,1047-1054. |
MLA | Liu, HQ,et al."Very High Cycle Fatigue Failure Mechanism of TC17 Alloy".ACTA METALLURGICA SINICA Vol.53 No.9(2017):1047-1054. |