Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process | |
Li, Shuangbin1,2; Yao, Ying1; Jia, Yongzhong1; Jing, Yan1; Sun, Jinhe1; Xie, Shaolei1 | |
刊名 | FERROELECTRICS
![]() |
2015-04-04 | |
卷号 | 478期号:1页码:127-131 |
关键词 | Tetragonal Phase Hexagonal Phase Barium Titanate Microstructure |
文献子类 | Article |
英文摘要 | BaTiO3 (BT) ceramics are prepared above 2000 degrees C by direct current arc discharge plasma process in argon atmosphere. The results show the formation of the perovskite structure. However, the coexisting of tetragonal phase and hexagonal phase is found in the structure. It is also found that a small amount of BaTi4O9 compound appears. With the sintering temperature increasing, the structure becomes more homogeneous because of interdiffusion of constituent ions and phase transition. The hexagonal phase gradually disappears and BaTi4O9 compound could also be traced. |
WOS关键词 | BARIUM-STRONTIUM-TITANATE ; DIELECTRIC-PROPERTIES ; POWDERS ; ROUTE |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
WOS记录号 | WOS:000355127700014 |
内容类型 | 期刊论文 |
源URL | [http://ir.isl.ac.cn/handle/363002/6134] ![]() |
专题 | 青海盐湖研究所_青海盐湖研究所知识仓储 青海盐湖研究所_盐湖资源综合利用工程技术中心 |
作者单位 | 1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Key Lab Salt Lake Resources & Chem, Xining, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Shuangbin,Yao, Ying,Jia, Yongzhong,et al. Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process[J]. FERROELECTRICS,2015,478(1):127-131. |
APA | Li, Shuangbin,Yao, Ying,Jia, Yongzhong,Jing, Yan,Sun, Jinhe,&Xie, Shaolei.(2015).Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process.FERROELECTRICS,478(1),127-131. |
MLA | Li, Shuangbin,et al."Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process".FERROELECTRICS 478.1(2015):127-131. |