Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage

CORC > 青海盐湖研究所 > 中国科学院青海盐湖研究所 > 青海盐湖研究所知识仓储

	Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage
	Zhang, Hongtao 1,3; Zhao, Youjing 1,2; Li, Jingli 1,2; Shi, Lijie 1,2; Wang, Min 1,2
刊名	HIGH TEMPERATURE MATERIALS AND PROCESSES
	2015-12-01
卷号	34 期号:8 页码:839-846
关键词	Solar Energy Materials Purification Thermal Properties Molten Nitrate Salts
文献子类	Article
英文摘要	This paper focuses on thermal stability of molten salts, operating temperature range and latent heat of molten salts at a high temperature. In this experiment, multi-component molten salts (purified Solar Salt) composed of purified NaNO3 and purified KNO3 were prepared by statical mixing method. Compared with unpurified Solar Salt, purified Solar Salt had a higher thermal stability. The optimal temperature would be increased from 500 degrees C to 550 degrees C, and the upper limitation temperature increases from 577.5 degrees C to 593.7 degrees C. Meanwhile, thermal stability and thermal cycling analysis showed the purified Solar Salt had a lower melting point and the deterioration time of molten salts was reduced. The melting point of purified Solar Salt decreases sharply to 223.8 degrees C and the latent heat increases from 74.39 J/g to 80.79 J/g. Besides, the XRD and chemical analysis test indicated that the degree of degradation reduced and the thermal storage efficiency of purified Solar Salt was improved.
WOS关键词	ENERGY-STORAGE ; PHASE-CHANGE ; GRAPHITE MATERIALS ; STABILITY ; SYSTEM ; KNO3/NANO3
WOS研究方向	Materials Science
语种	英语
WOS记录号	WOS:000365345700013
内容类型	期刊论文
源URL	[http://ir.isl.ac.cn/handle/363002/5322]
专题	青海盐湖研究所_青海盐湖研究所知识仓储中国科学院青海盐湖研究所
作者单位	1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China 2.Chinese Acad Sci, Key Lab Salt Lake Resources & Chem, Qinghai 810008, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Hongtao,Zhao, Youjing,Li, Jingli,et al. Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage[J]. HIGH TEMPERATURE MATERIALS AND PROCESSES,2015,34(8):839-846.
APA	Zhang, Hongtao,Zhao, Youjing,Li, Jingli,Shi, Lijie,&Wang, Min.(2015).Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage.HIGH TEMPERATURE MATERIALS AND PROCESSES,34(8),839-846.
MLA	Zhang, Hongtao,et al."Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage".HIGH TEMPERATURE MATERIALS AND PROCESSES 34.8(2015):839-846.