Universal Low-Temperature Process for Preparation of Multifunctional High-Performance Antireflective Mesoporous Silica Coatings on Transparent Polymeric Substrates

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 2018专题

	Universal Low-Temperature Process for Preparation of Multifunctional High-Performance Antireflective Mesoporous Silica Coatings on Transparent Polymeric Substrates
	Lu, Yuehui; Ai, Ling; Zhang, Jing; Li, Xiao; Zhang, Xianpeng; Song, Weijie
刊名	ACS APPLIED MATERIALS & INTERFACES
	2018
卷号	10 期号:5 页码:4993-4999
关键词	Strong Abrasion-resistance Sol-gel Method Polyimides Surface Nanoparticles Glass
英文摘要	In this work, we developed a universal low-temperature process for the preparation of multifunctional and robust mesoporous silica antireflective coatings on transparent polymeric substrates. The mesoporous, silica layer was formed after UV-O-3 exposure and ammonia vapor treatment,of dried: poly(ethylene glycol)-block-poly(propylene glycol)-block-poly(ethylene glycol) (F127)-containing acidic silica gel. The optical and antiscrubbing properties of the mesoporous silica coating were comparable to those of the coating prepared at 250 degrees C. The highest optical transmittance reached 99.55%, and the transmittance loss Was only 1.02% after 400 scrubbing cycles. The coating surface formed by the low-temperattire process was hydrophilic, resulting in excellent antifogging,properties. The, low-temperature process was successfully applied on various transparent polymeric substrates including polyimide, polyethylene terephthalate, polyethylene naphthalate, and polycarbonate. The excellent optical and mechanical performances of the mesoporous silica antireflective coatings on transparent polymeric substrates allow a wide rang of practical applications, especially in the field, of flexible electronics.
学科主题	Chemistry ; Science & Technology - Other Topics ; Materials Science
语种	英语
公开日期	2018-12-04
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/16819]
专题	2018专题
推荐引用方式 GB/T 7714	Lu, Yuehui,Ai, Ling,Zhang, Jing,et al. Universal Low-Temperature Process for Preparation of Multifunctional High-Performance Antireflective Mesoporous Silica Coatings on Transparent Polymeric Substrates[J]. ACS APPLIED MATERIALS & INTERFACES,2018,10(5):4993-4999.
APA	Lu, Yuehui,Ai, Ling,Zhang, Jing,Li, Xiao,Zhang, Xianpeng,&Song, Weijie.(2018).Universal Low-Temperature Process for Preparation of Multifunctional High-Performance Antireflective Mesoporous Silica Coatings on Transparent Polymeric Substrates.ACS APPLIED MATERIALS & INTERFACES,10(5),4993-4999.
MLA	Lu, Yuehui,et al."Universal Low-Temperature Process for Preparation of Multifunctional High-Performance Antireflective Mesoporous Silica Coatings on Transparent Polymeric Substrates".ACS APPLIED MATERIALS & INTERFACES 10.5(2018):4993-4999.