Selective reduction leaching of vanadium and iron by oxalic acid from spent V2O5-WO3/TiO2 catalyst | |
Wu, Wenfen1,2; Wang, Chenye1; Bao, Weijun1; Li, Huiquan1,2 | |
刊名 | HYDROMETALLURGY |
2018-08-01 | |
卷号 | 179页码:52-59 |
关键词 | Spent Scr Denitrification Catalyst Oxalic Acid Leaching Mechanism |
ISSN号 | 0304-386X |
DOI | 10.1016/j.hydromet.2018.05.021 |
英文摘要 | Large amounts of selective catalytic reduction (SCR) denitrification catalysts with poor mechanical property are disposed and difficult to be regenerated, resulting in environmental pollution. For spent SCR denitrification catalyst, the ratio of V4+ /V5+ decreased by about 45% and Fe impurity increased > 10 times, which influenced the recycling of the supporter. Selective leaching of V and Fe by oxalic acid and its reaction mechanism were investigated. Under the optimized leaching condition: oxalic acid concentration of 1.0 mol/L, reaction temperature of 90 degrees C, liquid-to-solid ratio of 20 mL/g, < 75 mu m particle size and leaching time of 180 min, the leaching efficiencies of V and Fe reached over 84% and 96%, respectively. The reaction mechanism for the selective leaching of these metals was determined through UV-VIS spectrophotometry and CO2 emission analyses. After dissolution and complexation, VO2+ and Fe3+ were reduced to water-soluble cations VO2+ and Fe3+. When V and Fe was in the specific forms of VOC2O4 and Fe(C2O4)(2)(2-). at 0.33 pH, high leaching efficiency was obtained. It indicated that redox reactions led to the broken of dissolution and complexation equilibriums for VO2+, VO+ and Fe3+. For W and Ti, only dissolution and complexation reactions occurred and the leaching efficiency was limited by the solubility. The leaching residue with anatase TiO2 was recovered as carrier and used for synthesis of a new SCR catalyst. |
资助项目 | National Natural Science Foundation of China[51574214] |
WOS关键词 | Ray Photoelectron-spectroscopy ; Commercial Scr Catalysts ; Titanium Slag ; Sulfuric-acid ; Recovery ; Regeneration ; Dissolution ; Tio2 ; Oxides ; Precipitation |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE BV |
WOS记录号 | WOS:000441644200007 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/25680] |
专题 | 中国科学院过程工程研究所 |
通讯作者 | Li, Huiquan |
作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, Natl Engn Lab Clean Prod Technol Hydromet, Key Lab Green Proc & Engn, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Wu, Wenfen,Wang, Chenye,Bao, Weijun,et al. Selective reduction leaching of vanadium and iron by oxalic acid from spent V2O5-WO3/TiO2 catalyst[J]. HYDROMETALLURGY,2018,179:52-59. |
APA | Wu, Wenfen,Wang, Chenye,Bao, Weijun,&Li, Huiquan.(2018).Selective reduction leaching of vanadium and iron by oxalic acid from spent V2O5-WO3/TiO2 catalyst.HYDROMETALLURGY,179,52-59. |
MLA | Wu, Wenfen,et al."Selective reduction leaching of vanadium and iron by oxalic acid from spent V2O5-WO3/TiO2 catalyst".HYDROMETALLURGY 179(2018):52-59. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论