Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests | |
Zhou, BJ; Wang, LY; Chen, B; Jia, YW; Wen, W; Li, DJ; Shu, D; Jin, PP; Zeng, XQ; Ding, WJ | |
刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING |
2017 | |
卷号 | 708期号:-页码:319-328 |
关键词 | Mg-re Alloys Magnesium Alloys Precipitate Morphology Phase Microstructure Fabrication Simulation Evolution |
ISSN号 | 0921-5093 |
DOI | 10.1016/j.msea.2017.10.011 |
文献子类 | 期刊论文 |
英文摘要 | Microstructure evolution of a supersaturated solid solution Mg-2.2 wt%Nd alloy during aging at 240 degrees C for 6 h (stage I), at 295 degrees C for 3 h (stage II), and finally at 320 degrees C for 1 h (stage III) was studied by in situ synchrotron X-Ray diffraction. In stage I, diffraction from beta(1) (Mg3Nd, FCC) precipitates was observed after similar to 15 min. Evolution of the volume, size, and aspect ratio of beta(1) with the aging time were estimated from peak intensity and peak width analysis. In stage II, diffraction from beta (Mg12Nd, tetragonal) precipitates was observed after similar to 36 min while beta(1) remained in the material. In stage III, the volume of h reduced substantially in relative to beta. The identified precipitation sequence from the in situ aging experiment is supported by ex situ electron microscopy observations. beta', which had not been detected by synchrotron X-rays, was additionally found using transmission electron microscopy in the material by the end of aging stage I. Tension and hardness tests using specimens with different aging conditions were further performed to understand how different precipitates affect the strength and ductility of the Mg-Nd alloy. |
WOS关键词 | MG-RE ALLOYS ; MAGNESIUM ALLOYS ; PRECIPITATE MORPHOLOGY ; PHASE ; MICROSTRUCTURE ; FABRICATION ; SIMULATION ; EVOLUTION |
语种 | 英语 |
WOS记录号 | WOS:000415770100033 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/28835] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Zhou, BJ,Wang, LY,Chen, B,et al. Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2017,708(-):319-328. |
APA | Zhou, BJ.,Wang, LY.,Chen, B.,Jia, YW.,Wen, W.,...&Ding, WJ.(2017).Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,708(-),319-328. |
MLA | Zhou, BJ,et al."Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 708.-(2017):319-328. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论