Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt | |
Zhu, HL; Holmes, R; Hanley, T; Davis, J; Short, K; Edwards, L; Li, ZJ | |
刊名 | CORROSION SCIENCE |
2017 | |
卷号 | 125期号:-页码:184-193 |
关键词 | Radiation-induced Segregation Behavior Nickel Diffusion Metals Kinetics |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2017.06.027 |
文献子类 | 期刊论文 |
英文摘要 | Samples of a Ni-Mo-Cr-Fe-Si alloy subject to helium ion irradiation damage were corroded in a eutectic mixture of FLiNaK at 750 degrees C. It was found that the helium bubbles that formed increased the number of surface defects so greatly increasing the physical contact area between the alloy and the molten salt, resulting in acceleration of corrosion damage. Segregation and depletion of chemical elements at bubble surfaces were also identified, and became more severe with increasing bubble size. Significant segregation of Si resulted in the formation of Ni-Si precipitates at large bubbles. This segregation enhanced the chemical corrosion damage to the alloy. |
WOS关键词 | RADIATION-INDUCED SEGREGATION ; BEHAVIOR ; NICKEL ; DIFFUSION ; METALS ; KINETICS |
语种 | 英语 |
WOS记录号 | WOS:000407535500018 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/28632] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Zhu, HL,Holmes, R,Hanley, T,et al. Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt[J]. CORROSION SCIENCE,2017,125(-):184-193. |
APA | Zhu, HL.,Holmes, R.,Hanley, T.,Davis, J.,Short, K.,...&Li, ZJ.(2017).Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt.CORROSION SCIENCE,125(-),184-193. |
MLA | Zhu, HL,et al."Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt".CORROSION SCIENCE 125.-(2017):184-193. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论