Corrosion behavior of TiC-SiC composite ceramics in molten FLiNaK salt | |
Gu, YF; Liu, JX; Wang, Y; Xue, JX; Wang, XG; Zhang, HB; Xu, FF; Zhang, GJ | |
刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY |
2017 | |
卷号 | 37期号:7页码:2575-2582 |
关键词 | Titanium Carbide Corrosion Behavior Silicon Carbide Molten Flinak Salt |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2017.02.020 |
文献子类 | 期刊论文 |
英文摘要 | Immersion corrosion tests of TiC0.(8), TiC, TiC-20 vol% SiC, TIC-40 vol% SiC and SiC have been performed in molten FLiNaK salt at 800 degrees C for 25-200 h under argon cover gas. All of these five samples showed small mass loss and relatively good corrosion resistance in molten FLiNaK salt. The corrosion patterns of TiC0.8, TiC, TiC-20 vol% SiC and TiC-40 vol% SiC were inter-granular corrosion, which were attributed to the depletion of Ti along the grain boundaries. SiC exhibited a general corrosion process in which a carbon rich layer formed on the surface, resulting from the depletion of Si. The carbon-rich layer protected SiC against further corrosion, hence lowering the corrosion rate. The corrosion results of TiC-20% SiC and TiC-40% SiC revealed the corrosion resistance of TiC could be improved by adding SiC. And the contribution of SiC to better corrosion resistance has been elucidated. (C) 2017 Elsevier Ltd. All rights reserved. |
语种 | 英语 |
WOS记录号 | WOS:000398753400004 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/27285] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Gu, YF,Liu, JX,Wang, Y,et al. Corrosion behavior of TiC-SiC composite ceramics in molten FLiNaK salt[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2017,37(7):2575-2582. |
APA | Gu, YF.,Liu, JX.,Wang, Y.,Xue, JX.,Wang, XG.,...&Zhang, GJ.(2017).Corrosion behavior of TiC-SiC composite ceramics in molten FLiNaK salt.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,37(7),2575-2582. |
MLA | Gu, YF,et al."Corrosion behavior of TiC-SiC composite ceramics in molten FLiNaK salt".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 37.7(2017):2575-2582. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论