Synthesis and luminescent behavior of Dy:Y3Ga5O12 phosphor for UV induced white LEDs | |
Zhu, L.; Guo, X. Y.; Sun, X. H.; Sai, Q. L.; Di, J. Q. | |
刊名 | Optik |
2017 | |
卷号 | 144页码:86 |
通讯作者 | dijuqing@mail.siom.ac.cn |
英文摘要 | The synthesis, X-ray diffraction (XRD) pattern, excitation spectrum, emission spectra and decay times were studied for the first time to our best knowledge. The Dy:Y3Ga5O12 (Dy:YGG) phosphors with Dy3+ ions concentration of 0.5%, 1%,3%, 5% and 10% were prepared by sol-gel method. The XRD patterns show that the phosphors possess perfect YGG phase. The average particle size of the Dy:YGG phosphors was calculated to be about 40 nm. The strongest excitation peak was 353 nm, which is favorable to ultra violet (UV) induced white light-emitting diodes (LEDs). Three emission bands centered at 480 nm, 580 nm and 672 nm could be observed under excitation of 353 nm. The yellow-to-blue integrated intensity ratios (Y/B) were 1.4-1.7 for the Dy3+ ions concentrations from 0.5 to 5%. The optimum Dy3+ concentration is 3%, and the corresponding 1931 Commission International de I'Eclairage (CIE) coordinates is (x=0.37, y = 0.38). The results show that Dy:YGG phosphors can be a good candidate for UV-excitation warm-yellowish-white LEDs. (C) 2017 Published by Elsevier GmbH. |
收录类别 | SCI |
资助信息 | China Postdoctoral Science Foundation [2016M592466]; Natural Science Foundation of Shanghai [15ZR1444700]; Guangdong Yang Fan Project |
WOS记录号 | WOS:000409150900013 |
内容类型 | 期刊论文 |
源URL | [http://ir.siom.ac.cn/handle/181231/28776] |
专题 | 上海光学精密机械研究所_其他 |
作者单位 | 中国科学院上海光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Zhu, L.,Guo, X. Y.,Sun, X. H.,et al. Synthesis and luminescent behavior of Dy:Y3Ga5O12 phosphor for UV induced white LEDs[J]. Optik,2017,144:86. |
APA | Zhu, L.,Guo, X. Y.,Sun, X. H.,Sai, Q. L.,&Di, J. Q..(2017).Synthesis and luminescent behavior of Dy:Y3Ga5O12 phosphor for UV induced white LEDs.Optik,144,86. |
MLA | Zhu, L.,et al."Synthesis and luminescent behavior of Dy:Y3Ga5O12 phosphor for UV induced white LEDs".Optik 144(2017):86. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论