Damage model of fresh concrete in sulphate environment | |
Zhang, JS; Zhang, YH; Feng, LP; Jin, DB; Wang, CC; Dong, QY; Zhang, JS (reprint author), Minist Educ, Key Lab Mech Disaster & Environm Western China, Lanzhou 730000, Peoples R China. | |
刊名 | JOURNAL OF CENTRAL SOUTH UNIVERSITY |
2015 | |
卷号 | 22期号:3页码:1104-1113 |
关键词 | fresh concrete sulphate corrosion corrosion coefficient computational model |
ISSN号 | 2095-2899 |
DOI | 10.1007/s11771-015-2622-7 |
文献子类 | Article |
英文摘要 | A model of damage to fresh concrete in a corrosive sulphate environment was formulated to investigate how and why the strength of corroded concrete changes over time. First, a corroded concrete block was divided into three regions: an expanded and dense region; a crack-development region; and a noncorroded region. Second, based on the thickness of the surface corrosion layer and the rate of loss of compressive strength of the corroding region, a computational model of the concrete blocks’ corrosion-resistance coefficient of compressive strength in a sulphate environment was generated. Third, experimental tests of the corrosion of concrete were conducted by immersing specimens in a corrosive medium for 270 d. A comparison of the experimental results with the computational formulae shows that the calculation results and test results are in good agreement. A parameter analysis reveals that the corrosion reaction plays a major role in the corrosion of fresh concrete containing ordinary Portland cement, but the diffusion of the corrosion medium plays a major role in the corrosion of concrete mixtures containing fly ash and sulphate-resistant cement. Fresh concrete with a high water-to-cement ratio shows high performance during the whole experiment process whereas fresh concrete with a low water-to-cement ratio shows poor performance during the late experiment period. |
学科主题 | Metallurgy & Metallurgical Engineering |
出版地 | HUNAN |
资助项目 | 国家自然科学基金项目 |
项目编号 | National Natural Science Foundation of China [51078176] ; Construction Science and Technology Research Project in Gansu Province, China [JK2010-58] |
语种 | 英语 |
CSCD记录号 | CSCD:5405592 |
WOS记录号 | WOS:000351290200039 |
资助机构 | NSFC ; GSSTD |
内容类型 | 期刊论文 |
源URL | [http://ir.lzu.edu.cn/handle/262010/144457] |
专题 | 土木工程与力学学院_期刊论文 |
通讯作者 | Zhang, JS (reprint author), Minist Educ, Key Lab Mech Disaster & Environm Western China, Lanzhou 730000, Peoples R China. |
推荐引用方式 GB/T 7714 | Zhang, JS,Zhang, YH,Feng, LP,et al. Damage model of fresh concrete in sulphate environment[J]. JOURNAL OF CENTRAL SOUTH UNIVERSITY,2015,22(3):1104-1113. |
APA | Zhang, JS.,Zhang, YH.,Feng, LP.,Jin, DB.,Wang, CC.,...&Zhang, JS .(2015).Damage model of fresh concrete in sulphate environment.JOURNAL OF CENTRAL SOUTH UNIVERSITY,22(3),1104-1113. |
MLA | Zhang, JS,et al."Damage model of fresh concrete in sulphate environment".JOURNAL OF CENTRAL SOUTH UNIVERSITY 22.3(2015):1104-1113. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论