INFLUENCE OF TANTALUM ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THE NIAL-BASED EUTECTIC ALLOY

CORC > 金属研究所 > 中国科学院金属研究所

	INFLUENCE OF TANTALUM ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THE NIAL-BASED EUTECTIC ALLOY
	Sheng, L. Y. ; Du, B. N. ; Lai, C. ; Guo, J. T. ; Xi, T. F.
刊名	STRENGTH OF MATERIALS
	2017
卷号	49 期号:1 页码:109-117
关键词	NiAl-based eutectic alloy tantalum Laves phase microstructure mechanical properties
ISSN号	0039-2316
通讯作者	Sheng, LY (reprint author), Peking Univ, Shenzhen Inst, Shenzhen, Peoples R China.
中文摘要	NiAl-28Cr-6Mo or NiAl-Cr(Mo) eutectic alloys with different degree of tantalum (Ta) addition have been fabricated and investigated. The microstructural characterization shows that minor Ta addition results in the formation of Cr2Ta Laves phase with C14 crystal structure. Small Laves phases are prone to precipitation along Cr(Mo) phase boundary, while large/bulk ones are formed in the intercellular region. As compared with the NiAl-Cr(Mo) eutectic alloy, minor Ta addition can refine Cr(Mo) and NiAl eutectic lamella in the core of eutectic cell but coarsen the Cr(Mo) and NiAl phase in the fringe of eutectic cell. An increased Ta addition invokes coarsening of Cr(Mo) and NiAl phases in the intercellular region and enhances Laves phase precipitation in the intercellular region. When the Ta addition increases to 2.0 at.%, the modified alloy mainly comprises ultrafine eutectic cell core and coarse Cr(Mo) and NiAl phases, which are semi-separated by NiAl dendritic and bulk Laves phase. The results confirm that the appropriate Ta addition can significantly improve the high-temperature strength with a feeble effect on room-temperature ductility, which can be ascribed to the microstructure optimization induced by the Ta addition. However, further Ta addition strongly affects the cellular eutectic microstructure and is detrimental for the roomtemperature ductility. The appropriate Ta content in the NiAl-Cr(Mo) eutectic alloy should be about 1.0 at.%.
学科主题	Materials Science, Characterization & Testing
收录类别	SCI
资助信息	Shenzhen International Cooperative Research Project [GJHZ20140419114548516]; Shenzhen Technology Innovation Plan [CXZZ20140731091722497, CXZZ20140419114548507]; China Postdoctoral Science Foundation [2015M580923]; Shenzhen Basic Research Project [JCYJ20140419114548515, JCYJ20150625155931806, JCYJ20160407090231002]
语种	英语
公开日期	2017-08-17
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/78359]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Sheng, L. Y.,Du, B. N.,Lai, C.,et al. INFLUENCE OF TANTALUM ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THE NIAL-BASED EUTECTIC ALLOY[J]. STRENGTH OF MATERIALS,2017,49(1):109-117.
APA	Sheng, L. Y.,Du, B. N.,Lai, C.,Guo, J. T.,&Xi, T. F..(2017).INFLUENCE OF TANTALUM ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THE NIAL-BASED EUTECTIC ALLOY.STRENGTH OF MATERIALS,49(1),109-117.
MLA	Sheng, L. Y.,et al."INFLUENCE OF TANTALUM ADDITION ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THE NIAL-BASED EUTECTIC ALLOY".STRENGTH OF MATERIALS 49.1(2017):109-117.