Electrochemical Behavior of Three 90Cu-10Ni Tubes from Different Manufacturers After Immersion in 3.5% NaCl Solution | |
Ekerenam, Okpo O. ; Ma, Aili ; Zheng, Yugui ; Emori, Wilfred | |
刊名 | JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE |
2017-04-01 | |
卷号 | 26期号:4页码:1701-1716 |
关键词 | corrosion and wear corrosion product film EIS nonferrous metals oxidation polarization curves XPS |
ISSN号 | 1059-9495 |
通讯作者 | Ma, AL (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 62 Wencui Rd, Shenyang 110016, Peoples R China. |
中文摘要 | Investigation on the electrochemical behavior and corrosion product films formed on three 90Cu-10Ni tubes designated as Tubes A, B and C from three different manufacturers with different service lives were carried out using electrochemical techniques, SEM, XRD and XPS after immersion in 3.5 wt.% NaCl solution. The results of polarization curve measurements showed noticeable decrease in the corrosion current densities (I (corr)) of the three tubes with immersion time, and the I (corr) of Tube C was comparatively lower than those of Tubes A and B at early immersion period. EIS measurements revealed duplex film layers on the surface of the samples with the inner film formation occurring at different times for different tubes as the film resistance R (f2) revealed the formation of the inner compact layer in Tube C after 15-day immersion and in Tubes A and B after 30 days. Tube C showed better corrosion resistance which is due to early formation of the inner compact oxide film. The XPS analysis revealed Ni enrichment on the surface film of the three samples but Ni depletion as the immersion time is increased. |
学科主题 | Materials Science, Multidisciplinary |
收录类别 | SCI |
资助信息 | National Natural Science Foundation of China [Y7F2131111]; National Environmental Corrosion Platform [2005DKA10400] |
语种 | 英语 |
公开日期 | 2017-08-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/78205] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Ekerenam, Okpo O.,Ma, Aili,Zheng, Yugui,et al. Electrochemical Behavior of Three 90Cu-10Ni Tubes from Different Manufacturers After Immersion in 3.5% NaCl Solution[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2017,26(4):1701-1716. |
APA | Ekerenam, Okpo O.,Ma, Aili,Zheng, Yugui,&Emori, Wilfred.(2017).Electrochemical Behavior of Three 90Cu-10Ni Tubes from Different Manufacturers After Immersion in 3.5% NaCl Solution.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,26(4),1701-1716. |
MLA | Ekerenam, Okpo O.,et al."Electrochemical Behavior of Three 90Cu-10Ni Tubes from Different Manufacturers After Immersion in 3.5% NaCl Solution".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE 26.4(2017):1701-1716. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论