Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti2AlNb Intermetallics

CORC > 金属研究所 > 中国科学院金属研究所

	Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti2AlNb Intermetallics
	Lu, Zheng-Guan ; Wu, Jie ; Guo, Rui-Peng ; Xu, Lei ; Yang, Rui
刊名	ACTA METALLURGICA SINICA-ENGLISH LETTERS
	2017-07-01
卷号	30 期号:7 页码:621-629
关键词	Ti2AlNb alloy Powder metallurgy Hot deformation Ring rolling
ISSN号	1006-7191
通讯作者	Xu, L (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
中文摘要	Powder metallurgy (PM) Ti-22Al-24Nb-0.5Mo (at.%) alloys were prepared by hot isostatic pressing. In order to study the feasibility of PM ? ring rolling combined process for preparing Ti2AlNb rings, thermal mechanical simulation tests of PM Ti2AlNb alloys were conducted and two rectangular PM rings (150 mm in height, 75 mm in thickness, 350 mm in external diameter) were rolled as a validation experiment. Experimental results show that the flow stress of Ti2AlNb alloys exhibited a significant drop at the very beginning of the deformation (true strain <0.1), and became stable with the increase in strain. Stress instability phenomenon of PM Ti2AlNb alloys was more obvious than that of wrought alloy. Flow stress fluctuation at the initial stage of deformation is related to phase transition of Ti2AlNb alloys which strongly depends on heat treatment and thermal mechanical deformation process. Processing windows during initial stage of ring rolling process is very crucial. A sound PM Ti2AlNb rectangular ring blank (height = 150 mm, thickness = 30 mm, external diameter = 750 mm) was successfully rolled in two passes by using the improved heat preservation method and optimized rolling parameters. Tensile properties of PM Ti2AlNb alloy were improved, and the porosity was reduced after ring rolling.
学科主题	Metallurgy & Metallurgical Engineering
收录类别	SCI
语种	英语
公开日期	2017-08-17
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/78057]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Lu, Zheng-Guan,Wu, Jie,Guo, Rui-Peng,et al. Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti2AlNb Intermetallics[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2017,30(7):621-629.
APA	Lu, Zheng-Guan,Wu, Jie,Guo, Rui-Peng,Xu, Lei,&Yang, Rui.(2017).Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti2AlNb Intermetallics.ACTA METALLURGICA SINICA-ENGLISH LETTERS,30(7),621-629.
MLA	Lu, Zheng-Guan,et al."Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti2AlNb Intermetallics".ACTA METALLURGICA SINICA-ENGLISH LETTERS 30.7(2017):621-629.