铝化与白金铝化涂层对MAR-M247镍基超合金之抗热腐蚀性质影响研究; Effects of Aluminide and Platinum-Aluminide Coatings on the Hot Corrosion Behavior of MAR-M247 Nickel-Based Superalloy | |
李义刚 ; 蔡文达 ; 李汝桐 ; I.K. Lee~ | |
刊名 | http://electrochem.xmu.edu.cn/CN/abstract/abstract8913.shtml
![]() |
2005-08-28 | |
关键词 | 镍基超合金 热腐蚀 铝化涂层 白金铝化涂层 Nickel-based superalloy Hot corrosion Aluminide coating Platinum-aluminide coating |
英文摘要 | 本文研究MAR-M247镍基超合金表面经铝化涂层或白金铝化涂层处理后,其热腐蚀效应对腐蚀速率与显微组织之影响,并藉试片质量增加量的变化评估抗热腐蚀的能力.铝化涂层之主要组成为-βN iA l相,而白金铝化涂层表面的主要组成为PtA l2相,利用盐喷覆法将Na2SO4被覆在试片表面,置于热处理炉中观测其热腐蚀性.实验得知,铝化涂层和白金铝化涂层均可明显抑制MAR-M247的热腐蚀,且后者之效果更明显,此两种涂层在910℃之Na2SO4环境中的抗蚀性均较MAR-M247合金为佳.; This study is to investigate the high temperature hot corrosion behavior of aluminide coating and platinum-aluminide coating on Ni-base superalloy MAR-M247. On the platinum-aluminide, aluminide and the base metal, respectively, by the salt spraying method. The resistances to hot corrosion of platinum-aluminide coating, aluminide coating and the base metal were evaluated by the variations of weight gains. Aluminide and platinum-aluminide coating showed significanty beneficial effect on inhibiting the hot corrosion of MAR-M247. But that of the platinum-aluminide coating was even much better. The aluminide coating surface was composed of β-NiAl, and that of the platinum-aluminide coating was PtAl_(2). Both two phases could provide better resistances to hot corrosion than that of MAR-M247 in Na_(2)SO_(4), at 910℃.; 作者联系地址:中山科学研究院飞弹火箭研究所,成功大学材料科学及工程学系,成功大学材料科学及工程学系 台湾台北 ,台湾台南 ,台湾台南; Author's Address: *1 ,W.T. Tasi~2,J.T. Lee~21. Missile and Rocket Systems Research Division, Chung-Shan Institute of Science & Technology,Taiwan,China;2. Department of Materials Engineering, Cheng-Kung University,Taiwan,China |
语种 | 中文 |
出版者 | 厦门大学《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/57897] ![]() |
专题 | 2005年第11卷 |
推荐引用方式 GB/T 7714 | 李义刚,蔡文达,李汝桐,等. 铝化与白金铝化涂层对MAR-M247镍基超合金之抗热腐蚀性质影响研究, Effects of Aluminide and Platinum-Aluminide Coatings on the Hot Corrosion Behavior of MAR-M247 Nickel-Based Superalloy[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8913.shtml,2005. |
APA | 李义刚,蔡文达,李汝桐,&I.K. Lee~.(2005).铝化与白金铝化涂层对MAR-M247镍基超合金之抗热腐蚀性质影响研究.http://electrochem.xmu.edu.cn/CN/abstract/abstract8913.shtml. |
MLA | 李义刚,et al."铝化与白金铝化涂层对MAR-M247镍基超合金之抗热腐蚀性质影响研究".http://electrochem.xmu.edu.cn/CN/abstract/abstract8913.shtml (2005). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论