碳钢在生物膜和硫化物膜下的电化学腐蚀行为

CORC > 厦门大学 > 2001年第7卷

	碳钢在生物膜和硫化物膜下的电化学腐蚀行为; Electrochemistry Characteristic of Carbon Steel under Biofilm and Sulfide Film
	董泽华 ; 郭兴蓬 ; 郑家燊 ; 许立铭 ; DONG Ze_hua ; GUO Xing_peng ; ZHENG Jia_shen ; XU Li_ming
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract9260.shtml
	2001-05-28
关键词	生物膜硫酸盐还原菌碳钢丝束电极面电位/电流分布电化学阻抗谱 Biofilm SRB Carbon Steel Wire Beam Electrode Mapping EIS
英文摘要	应用丝束电极技术比较了SRB生物膜以及硫化物膜对Q2 35碳钢腐蚀过程的影响机制 ,采用电位、电流扫描技术测试了生物膜和FeS膜下的碳钢腐蚀不均匀性特征 ,发现由于膜的导电性致使表面电位扫描已不能作为膜下局部腐蚀的判据 .动电位扫描表明无氧近中性溶液中 ,硫化物膜对碳钢具有一定保护作用 .电化学阻抗谱显示 ,硫化物膜电容增加缓慢 ,其极化电阻Rp 随时间呈先增后降的趋势 .与硫化物膜相比 ,生物膜表现出极大的电容 (10 4 ～ 10 5μF/cm2 ) ,且膜电容随时间呈S型增加 ,而极化电阻Rp 则呈指数下降 ,由此可知生物膜加速了腐蚀; Wire Beam Electrode (WBE) made of Q235 carbon steel was applied to study the heterogeneous corrosion beneath biofilm formed by Sulfate Reducing Bacteria (SRB) in culture and sulfide film in solution with 1% NaCl and 300 mg/L S 2- . The potential,galvanic density mapping,as well as polarization curve and Electrochemical Impedance Spectrum (EIS) were measured to predict the localized corrosion under biofilm and sulfide film.As a result,the mapping showed the potential fluctuation on the WBE surface decreased over time due to the conductivity of the biofilm and sulfide film.Therefore,the potential mapping could not be a criterion of localized corrosion under biofilm.Instead,the current mapping could give a good prediction to the MIC.The sulfide film could inhibit corrosion of carbon steel.However,the biofilm accelerate the corrosion.Polarization resistance R p increased over time in the Na 2S solution if lack of O 2.In addition,the biofilm capacity moved up to a very large level (～10 5 μF/cm 2)in shape of Sigmoid with its polarization resistance decreasing exponentially when SRB grew.; 作者联系地址：华中科技大学化学系!湖北武汉430074,华中科技大学化学系!湖北武汉430074,华中科技大学化学系!湖北武汉430074,华中科技大学化学系!湖北武汉430074; Author's Address: Dept. of Chem.,Huazhong Univ. of Science and Technology,Wuhan 430074,China
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/57604]
专题	2001年第7卷
推荐引用方式 GB/T 7714	董泽华,郭兴蓬,郑家燊,等. 碳钢在生物膜和硫化物膜下的电化学腐蚀行为, Electrochemistry Characteristic of Carbon Steel under Biofilm and Sulfide Film[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract9260.shtml,2001.
APA	董泽华.,郭兴蓬.,郑家燊.,许立铭.,DONG Ze_hua.,...&XU Li_ming.(2001).碳钢在生物膜和硫化物膜下的电化学腐蚀行为.http://electrochem.xmu.edu.cn/CN/abstract/abstract9260.shtml.
MLA	董泽华,et al."碳钢在生物膜和硫化物膜下的电化学腐蚀行为".http://electrochem.xmu.edu.cn/CN/abstract/abstract9260.shtml (2001).