| 题名 | 喷雾干燥—高温热处理法制备YAG: Ce3+ 荧光粉及其性能研究; Preparation and Study of the Performance of YAG: Ce3+ Phosphor by Spray Drying and then Heat Treatment at High Temperature |
| 作者 | 陈少云 |
| 答辩日期 | 2011 ; 2010 |
| 导师 | 曾人杰 |
| 关键词 | 聚合铝阳离子 喷雾干燥 钇铝石榴石 LED aluminum polycation spray drying YAG LED |
| 英文摘要 | 白光发光二极管（LED）无污染、节能、寿命长、体积小、发热小，被认为是21世纪最有价值的新光源。铈激活钇铝石榴石（YAG:Ce3+）黄色荧光粉，与掺In氮化镓蓝光芯片组合成白光LED，是目前的主流。 工业上制备荧光粉目前多采用高温固相法；但该方法合成温度高，易造成粉末团聚，研磨后颗粒破碎、表面玻璃态增多，影响到发光亮度等指标。喷雾法能在一定程度上解决粉末团聚的问题。本研究分别采用钇铈草酸盐悬浊液和含聚合铝阳离子的悬浊液，经喷雾干燥—高温热处理，制备YAG:Ce3+荧光粉。 本文系统研究了钇铈草酸盐悬浊液喷雾干燥—高温热处理法制备YAG:Ce3+荧光粉的工艺过程，研究了沉淀剂种类、热处理温度...; White light-emitting diode (LED) is recognized as the most valuable new lighting source in 21st century because of its excellent properties, such as non-pollution, energy saving, long lasting life, small size and less heat. It is the mainstream to form white LED that the yellow Ce-doping yttrium aluminum garnet phosphor is combined with the blue In-doping GaN LED chip. In industry, the phosphor i...; 学位：工学硕士; 院系专业：材料学院材料科学与工程系_材料学; 学号：20720071150001 |
| 语种 | zh_CN |
| 出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=28270 |
| 内容类型 | 学位论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/21949]  |
| 专题 | 材料学院－学位论文 |
| 推荐引用方式 GB/T 7714 | 陈少云. 喷雾干燥—高温热处理法制备YAG: Ce3+ 荧光粉及其性能研究, Preparation and Study of the Performance of YAG: Ce3+ Phosphor by Spray Drying and then Heat Treatment at High Temperature[D]. 2011, 2010. |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论