| 题名 | 流延法制备低介电损耗巨电容率CaCu3Ti4O12陶瓷及其电性能研究; Preparation and Properties of CaCu3Ti4O12 Ceramics with Giant Permittivity and Low Dielectric Loss via Tape Casting |
| 作者 | 李伟 |
| 答辩日期 | 2014 ; 2014 |
| 导师 | 熊兆贤 |
| 关键词 | 钛酸铜钙 低介电损耗 流延法 表面效应 CaCu3Ti4O12 Low dielectric loss Tape Casting SBLC |
| 英文摘要 | 本论文在固相反应法的基础上结合流延成型制备CaCu3Ti4O12（简称CCTO）陶瓷薄片，研究两步法烧结和Cu不同化学计量比对流延成型CCTO陶瓷致密度、微观结构和电学性能等方面影响；同时对CCTO陶瓷介电机理的表面效应进行初步探讨；成功制备多层CCTO陶瓷基双功能元件，并与铝电解电容器和超级电容器进行性能和充放电特性对比试验。 首先，采用两步法烧结流延成型CCTO陶瓷薄片。第二步保温时间和第二步烧结温度对流延成型CCTO陶瓷的性能都有较大的影响。随着第二步保温时间的延长和第二步烧结温度的升高，CCTO陶瓷的相对密度和电容率都有所提高。在第二步烧结温度1000℃保温72h烧结的CCTO陶瓷，...; In this paper, CaCu3Ti4O12, i.e., CCTO, ceramics were prepared by the conventional solid-state reaction combining with tape casting. Effects of two-step sintering and excess of copper on density, micro-structure, and electric properties of the samples were studied. And the surface effect of CCTO ceramics was also investigated. And multilayer CCTO ceramics capacitors with twin functions were manufa...; 学位：工学硕士; 院系专业：材料学院_材料学; 学号：20720111150070 |
| 语种 | zh_CN |
| 出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=46545 |
| 内容类型 | 学位论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/80637]  |
| 专题 | 材料学院－学位论文 |
| 推荐引用方式 GB/T 7714 | 李伟. 流延法制备低介电损耗巨电容率CaCu3Ti4O12陶瓷及其电性能研究, Preparation and Properties of CaCu3Ti4O12 Ceramics with Giant Permittivity and Low Dielectric Loss via Tape Casting[D]. 2014, 2014. |