| 18/8型不锈钢在受力形变条件下腐蚀电化学行为的研究; Electrochemical Behaviors of the Loaded Stainless Steel in Dilute Thiosulphate Solution | |
| 林昌健 ; 冯祖德 ; 林福龄 ; 王发扬 ; 谭建光 ; 王元辉 | |
| 1995 | |
| 关键词 | 不锈钢 受力 电化学行为 应力腐蚀开裂 Stainless steel Stress corrosion cracking Electrochemical behavior |
| 英文摘要 | 应用电化学稳态技术、电化学交流阻抗、微区电化学技术及扫描电镜等方法，研究18/8型不锈钢在nA＿2S＿2O＿3稀溶液中，受外力形变条件下的腐蚀电化学行为.结果表明：力学因素可使表面腐蚀电化学活性增加；表面微裂纹的发生、消失和再钝化的动态过程，同时受电位和拉应力的影响；点腐蚀可优先发生在应力集中位置，点蚀的发展可能诱导不锈钢的应力腐蚀开裂.; The electrochemical behavior of l8/8 stainless steel in dilute thiosulphate solutionduring strained loading was studied by various electrochemical techniques and scanning electronmicroscope.It is evidenced that the corrosion activity of stainless steel increased with strained loading.The dynamic process of repassivation ,which may datermine the initiation ,the cease and developmentof the stress corrosion cracking For stainless steel ,was strongly inFluenced by both electrochemical andloading conditions.Pitting corrosion may locate preFerentially on the sites which was suFFered mostloading.The propagation of pitting corrosion of stainless steel may induce stress corrosion crakingunder certain conditions.; 国家自然科学基金;固体表面物理化学国家重点实验室开放课题 |
| 语种 | zh_CN |
| 内容类型 | 期刊论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/106176]  |
| 专题 | 化学化工－已发表论文 |
| 推荐引用方式 GB/T 7714 | 林昌健,冯祖德,林福龄,等. 18/8型不锈钢在受力形变条件下腐蚀电化学行为的研究, Electrochemical Behaviors of the Loaded Stainless Steel in Dilute Thiosulphate Solution[J],1995. |
| APA | 林昌健,冯祖德,林福龄,王发扬,谭建光,&王元辉.(1995).18/8型不锈钢在受力形变条件下腐蚀电化学行为的研究.. |
| MLA | 林昌健,et al."18/8型不锈钢在受力形变条件下腐蚀电化学行为的研究".(1995). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论