	7A12-T7352铝合金高温力学性能及断裂行为研究
	黄敏 ; 陈轶 ; 李超 ; 陈军洲 ; 汝继刚 ; HUANG Min ; CHEN Yi ; LI Chao ; CHEN Jun-zhou ; RU Ji-gang
	2016-03-30 ; 2016-03-30
关键词	7A12 高温力学行为 微观组织 7A12 high temperature mechanical properties microstructure TG146.21
其他题名	High Temperature Mechanical Properties and Fracture Characteristics of 7A12-T7352
中文摘要	研究了7A12-T7352铝合金在室温~175℃温度范围内的拉伸性能及断裂行为。利用SEM,TEM分析合金经不同温度拉伸测试后的显微组织及断口形貌。结果表明:随试验的温度升高,7A12-T7352合金的拉伸强度逐渐降低,伸长率呈先增加后降低的变化趋势;7A12-T7352合金在高温拉伸过程中,析出相相对稳定,未发生明显长大;随试验的温度升高,断口中高温滑移特征以及基体/沉淀相界面的滑脱越来越显著,试验温度对7A12-T7352合金的变形、断裂特征有显著影响。; The effect of temperature in range of room temperature- 175℃ on mechanical properties and fracture characteristics of 7A12-T7352 was investigated. The microstructures and fracture surfaces were analyzed by using TEM and SEM. The results show that the tensile strength in area is temperature-dependent and decreased with increasing the temperature. The microstructures of precipitates and grain size show nearly stable in high temperature tensile as investigated by TEM. Furthermore,there is remarkable effect slip characteristics and interface of slippage with increasing the temperature from fracture feature.
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/144527]
专题	清华大学
推荐引用方式 GB/T 7714	黄敏,陈轶,李超,等. 7A12-T7352铝合金高温力学性能及断裂行为研究[J],2016, 2016.
APA	黄敏.,陈轶.,李超.,陈军洲.,汝继刚.,...&RU Ji-gang.(2016).7A12-T7352铝合金高温力学性能及断裂行为研究..
MLA	黄敏,et al."7A12-T7352铝合金高温力学性能及断裂行为研究".(2016).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。