Excellent tribological behavior of hexadecylphosphonic acid films formed on titanium alloy | |
ZHANG CaiXia ; LIU YuHong ; WEN ShiZhu ; ZHANG CaiXia ; LIU YuHong ; WEN ShiZhu | |
2016-03-30 ; 2016-03-30 | |
关键词 | Ti6Al4V hexadecylphosphonic acid tribological properties surface modification polytetrafluoroethylene TG174.4 |
其他题名 | Excellent tribological behavior of hexadecylphosphonic acid films formed on titanium alloy |
中文摘要 | Titanium alloy(Ti6Al4V)surfaces are generally modified to achieve some specific surface properties to satisfy requirements of clinical medicine.In our work,hexadecylphosphonic acid(HDPA)films were successfully formed on Ti6Al4V and subsequently confirmed by X-ray photoelectron spectroscopy(XPS)and atomic force microscopy(AFM)measurements.The tribological properties of the HDPA-modified Ti6Al4V were investigated using a ball-on-disk tribometer with a linear reciprocating movement.Experimental results indicate that the HDPA-modified Ti6Al4V can maintain a low friction coefficient(approximately 0.06)for 4 h when sliding against polytetrafluoroethylene(PTFE)balls under a load of 0.8 N in comparison to bare Ti6Al4V(approximately 0.2);the friction coefficient of the HDPA-modified Ti6Al4V shows a 70%decline.In addition,the wear rate of PTFE balls sliding against bare Ti6Al4V was almost twenty times that of PTFE balls sliding against the HDPA-modified Ti6Al4V.Moreover,results of tribological experiments for different speeds(from 3 to 24 mm/s)and loads(from 0.8 to 3.2 N)proved that the HDPA-modified Ti6Al4V was not sensitive to both velocity and load.The friction coefficients were still low and stable even under a high load of 3.2 N or at a high speed of 24 mm/s.This indicates that this soft modification is an optional method of improving tribological properties of Ti6Al4V.; Titanium alloy(Ti6Al4V)surfaces are generally modified to achieve some specific surface properties to satisfy requirements of clinical medicine.In our work,hexadecylphosphonic acid(HDPA)films were successfully formed on Ti6Al4V and subsequently confirmed by X-ray photoelectron spectroscopy(XPS)and atomic force microscopy(AFM)measurements.The tribological properties of the HDPA-modified Ti6Al4V were investigated using a ball-on-disk tribometer with a linear reciprocating movement.Experimental results indicate that the HDPA-modified Ti6Al4V can maintain a low friction coefficient(approximately 0.06)for 4 h when sliding against polytetrafluoroethylene(PTFE)balls under a load of 0.8 N in comparison to bare Ti6Al4V(approximately 0.2);the friction coefficient of the HDPA-modified Ti6Al4V shows a 70%decline.In addition,the wear rate of PTFE balls sliding against bare Ti6Al4V was almost twenty times that of PTFE balls sliding against the HDPA-modified Ti6Al4V.Moreover,results of tribological experiments for different speeds(from 3 to 24 mm/s)and loads(from 0.8 to 3.2 N)proved that the HDPA-modified Ti6Al4V was not sensitive to both velocity and load.The friction coefficients were still low and stable even under a high load of 3.2 N or at a high speed of 24 mm/s.This indicates that this soft modification is an optional method of improving tribological properties of Ti6Al4V. |
语种 | 英语 ; 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/144432] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | ZHANG CaiXia,LIU YuHong,WEN ShiZhu,et al. Excellent tribological behavior of hexadecylphosphonic acid films formed on titanium alloy[J],2016, 2016. |
APA | ZHANG CaiXia,LIU YuHong,WEN ShiZhu,ZHANG CaiXia,LIU YuHong,&WEN ShiZhu.(2016).Excellent tribological behavior of hexadecylphosphonic acid films formed on titanium alloy.. |
MLA | ZHANG CaiXia,et al."Excellent tribological behavior of hexadecylphosphonic acid films formed on titanium alloy".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论