	硫酸钠/氧化硅复合定形相变材料的溶胶凝胶法制备和表征(英文)
	郭强 ; 王涛 ; GUO Qiang ; WANG Tao
	2016-03-30 ; 2016-03-30
关键词	sodium sulfate silicon dioxide phase change material shape-stabilized sol-gel method TQ427.26
其他题名	Preparation and Characterization of Sodium Sulfate/Silica Composite as a Shape-stabilized Phase Change Material by Sol-gel Method
中文摘要	A sodium sulfate(Na2SO4)/silica(SiO2) composite was prepared as a shape-stabilized solid-liquid phase change material by a sol-gel procedure using Na2SiO3 as the silica source. Na2SO4 in the composite acts as a latent heat storage substance for solid-liquid phase change, while SiO2 acts as a support material to provide structural strength and prevent leakage of melted Na2SO4. The microstructure and composition of the prepared composite were characterized by the N2 adsorption, transmission electron microscope(TEM), scanning electron microscope(SEM), Fourier transform infrared spectroscopy(FTIR) and X-ray diffraction. The results show that the prepared Na2SO4/SiO2 composite is a nanostructured hybrid of Na2SO4 and SiO2 without new substances produced during the phase change. The macroscopic shape of the Na2SO4/SiO2 composite after the melting and freezing cycles does not change and there is no leakage of Na2SO4. Determined by differential scanning calorimeter(DSC) analysis, the values of phase change latent heat of melting and freezing of the prepared Na2SO4/SiO2(50%, by mass) composite are 82.3 kJ穔g?1 and 83.7 kJ穔g?1, and temperatures of melting and freezing are 886.0 癈 and 880.6 癈, respectively. Furthermore, the Na2SO4/SiO2 composite maintains good thermal energy storage and release ability even after 100 cycles of melting and freezing. The satisfactory thermal storage performance renders this composite a versatile tool for high-temperature thermal energy storage.; A sodium sulfate(Na2SO4)/silica(SiO2) composite was prepared as a shape-stabilized solid-liquid phase change material by a sol-gel procedure using Na2SiO3 as the silica source. Na2SO4 in the composite acts as a latent heat storage substance for solid-liquid phase change, while SiO2 acts as a support material to provide structural strength and prevent leakage of melted Na2SO4. The microstructure and composition of the prepared composite were characterized by the N2 adsorption, transmission electron microscope(TEM), scanning electron microscope(SEM), Fourier transform infrared spectroscopy(FTIR) and X-ray diffraction. The results show that the prepared Na2SO4/SiO2 composite is a nanostructured hybrid of Na2SO4 and SiO2 without new substances produced during the phase change. The macroscopic shape of the Na2SO4/SiO2 composite after the melting and freezing cycles does not change and there is no leakage of Na2SO4. Determined by differential scanning calorimeter(DSC) analysis, the values of phase change latent heat of melting and freezing of the prepared Na2SO4/SiO2(50%, by mass) composite are 82.3 kJ穔g?1 and 83.7 kJ穔g?1, and temperatures of melting and freezing are 886.0 癈 and 880.6 癈, respectively. Furthermore, the Na2SO4/SiO2 composite maintains good thermal energy storage and release ability even after 100 cycles of melting and freezing. The satisfactory thermal storage performance renders this composite a versatile tool for high-temperature thermal energy storage.
语种	英语 ; 英语
内容类型	期刊论文
源URL	[http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/144026]
专题	清华大学
推荐引用方式 GB/T 7714	郭强,王涛,GUO Qiang,等. 硫酸钠/氧化硅复合定形相变材料的溶胶凝胶法制备和表征(英文)[J],2016, 2016.
APA	郭强,王涛,GUO Qiang,&WANG Tao.(2016).硫酸钠/氧化硅复合定形相变材料的溶胶凝胶法制备和表征(英文)..
MLA	郭强,et al."硫酸钠/氧化硅复合定形相变材料的溶胶凝胶法制备和表征(英文)".(2016).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。